Polymer Property : Flexural Yield Strength = 8410 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	58.0 MPa	8410 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Cycolac® INP630 ABS INP630 is a specialty polymer that increases the service temperature of products. Can be used with a impact modifier to provide impact strength as well as high heat resistance. Provides excellent hi..
Flexural Yield Strength	58.0 MPa	8410 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Cycolac® INP630 ABS+SAN INP630 is a specialty polymer that increases the service temperature of products. Can be used with a impact modifier to provide impact strength as well as high heat resistance. Provides excellent hi..
Flexural Yield Strength	58.0 MPa	8410 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics GELOY CR7020 ASA ASA copolymer. Profile/sheet coextrusion over ABS. Excellent weatherability, good flow/aesthetics and high impact.
Flexural Yield Strength	58.0 MPa	8410 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics GELOY CR7020 ASA (Asia Pacific) ASA copolymer. Profile/sheet coextrusion over ABS. Excellent weatherability, good flow/aesthetics and high impact.
Flexural Yield Strength	58.0 MPa	8410 psi	ASTM D790
Rotuba H3 Cellulose Acetate Property values at 50% RH.Data provided by the manufacturer.
Flexural Yield Strength	58.0 MPa	8410 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics GELOY CR7520 ASA General purpose ASA. Excellent weatherability, good flow/aesthetics and high impact. Rated F2 by UL.
Flexural Yield Strength	58.0 MPa	8410 psi	ASTM D790
Ineos Nova 3601 General Purpose Crystal Polystyrene (discontinued **) Easy flow for high productivity, excellent post molding scuff resistanceApplications: Medical, LabwareExposure to gamma radiation in the 2.02-6.06 megarad range has no significant effect on the phys..
Flexural Yield Strength	58.0 MPa @Strain 3.50 %	8410 psi @Strain 3.50 %	ISO 178
FKuR Kunststoff BiogradeÂ® C 6530 Biodegradable Plastic Compound BIOGRADEÂ® are easy to process blends based on cellulose. BIOGRADEÂ® is composed mainly of natural resources. Based on cellulose, a product of the paper industry BIOGRADEÂ® has been especial..
Flexural Yield Strength	58.0 MPa	8410 psi	ASTM D790
Washington Penn PPUP4G402 Polypropylene, 40% Talc Filled, High Flow Exceptional retention of mechanical properties and appearance upon long term heat aging.Applications: Appliance parts.Data provided by Washington Penn Plastic Co., Inc.
Flexural Yield Strength	58.0 MPa	8410 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics GELOY CR7520 ASA (Asia Pacific) ASA copolymer. Automotive grilles and exteriors. Excellent weatherability, good flow/aesthetics and high impact. Rated f2 by UL.