SABIC Innovative Plastics Cycolac® INP630 ABS+SAN

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycolac®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycolac® INP630 ABS+SAN.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
INP630 is a specialty polymer that increases the service temperature of products. Can be used with a impact modifier to provide impact strength as well as high heat resistance. Provides excellent high heat resistance in thermoplastic polymers. Offers excellent flow properties in outdoor applications.
Physical Properties Metric English Comments
Specific Gravity 1.09 g/cc
1.09 g/cc
ASTM D792
Density 1.09 g/cc
0.0394 lb/in³
ISO 1183
Melt Flow 10.9 g/10 min

@Load 3.80 kg,
Temperature 230 °C
10.9 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D1238
21 g/10 min

@Load 10.0 kg,
Temperature 220 °C
21 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ISO 1133
Mechanical Properties Metric English Comments
Flexural Yield Strength 58.0 MPa
8410 psi
2 mm/min; ISO 178
115 MPa
16700 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 3.62 GPa
525 ksi
2 mm/min; ISO 178
3.88 GPa
563 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.190 J/cm
0.356 ft-lb/in
ASTM D256
0.130 J/cm

@Temperature -30.0 °C
0.244 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 3.00 kJ/m²
1.43 ft-lb/in²
80*10*4; ISO 180/1A
1.00 kJ/m²

@Temperature -30.0 °C
0.476 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 0.100 J/cm²
0.476 ft-lb/in²
ISO 179/2C
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 110 °C

@Thickness 3.20 mm
230 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 99.0 °C
210 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
100 °C

@Thickness 3.20 mm
212 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 116 °C
241 °F
Rate B/50; ISO 306
118 °C
244 °F
Rate B/120; ISO 306
Optical Properties Metric English Comments
Yellow Index 6.0 %
6.0 %
ASTM D1925