Polymer Property : Flexural Yield Strength = 80.4 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	80.4 MPa @Thickness 3.20 mm	11700 psi @Thickness 0.126 in	15mm/min; ASTM D790
LG Chemical LI970HF Co-Extrusion ASA Description: Good Weatherability, Scratch Resistance, High FlowApplication: Window Profile, Siding, Rain GutterCAS: 26299-47-8Information provided by LG Chemical
Flexural Yield Strength	80.4 MPa @Thickness 3.20 mm	11700 psi @Thickness 0.126 in	15 mm/min; ASTM D790
LG Chemical RS650 ABS Feature: Extrusion Molding, General PurposeApplication: MiscellaneousCAS No. 9003-56-9Information provided by LG Chemical
Flexural Yield Strength	80.4 MPa @Thickness 3.20 mm	11700 psi @Thickness 0.126 in	15 mm/min; ASTM D790
LG Chemical RS657 ABS, Chemical Resistance to Cyclopentane Feature: Extrusion Molding, Chemical Resistance to Cyclopentane, Thin ThicknessApplication: Refrigerator Inner LinerCAS No. 9003-56-9Information provided by LG Chemical
Flexural Yield Strength	80.4 MPa @Thickness 3.20 mm	11700 psi @Thickness 0.126 in	15 mm/min; ASTM D790
LG Chemical XR440 ABS, Low Emission High Heat ABS Feature: Injection Molding Grade, Low Emission High Heat ABSApplication: Automotives Interior housingCAS No. 25120-20-1, 9003-56-9, 25747-74-7, and 31621-07-5Information provided by LG Chemical
Flexural Yield Strength	80.4 MPa	11700 psi	ASTM D790
Samyang TribitÂ® 1501N PBT, Flame Retardancy Crystallization is fast, formability is excellent and thermal resistance, chemical resistance, electrical properties and abrasion resistance are excellent.1501N is a V-2 flame retardancy grade.Appli..
Flexural Yield Strength	80.4 MPa	11700 psi	ASTM D790
Samyang TribitÂ® 1503 Polybutylene Terephthalate Characteristics:High flow & processabilityApplications:AutomotiveConnectorGearOutdoor handleIgnition systemElectronicConnectorGas valveCoil bobbinSwitch caseRelay caseO/A partsAll information provid..
Flexural Yield Strength	80.4 MPa	11700 psi	ASTM D790
Samyang TrirexÂ® 3015NF Polycarbonate, Flame Retardancy PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3015NF is a flame retardant grade.Applications: Mobile Phone - battery caseInformation..
Flexural Yield Strength	80.4 MPa @Thickness 6.40 mm	11700 psi @Thickness 0.252 in	5 mm/min; ASTM D790
Bhansali Engineering Abstron IM14GL ABS Injection Molding Grade Super High Rigidity, Medium Impact, High Chemical ResistanceInformation provided by Bhansali
Flexural Yield Strength	80.4 MPa @Thickness 6.40 mm	11700 psi @Thickness 0.252 in	ASTM D-790
Bhansali Engineering Abstron IMG-1115 Glass Reinforced Grade Glass Reinforced ABS & SAN Resins for product specific requirement of very high rigidity and temperatureInformation provided by Bhansali
Flexural Yield Strength	80.4 MPa @Thickness 6.40 mm	11700 psi @Thickness 0.252 in	ASTM D-790
Bhansali Engineering Abstron IMG-1115 Glass Reinforced Grade Glass Reinforced ABS & SAN Resins for product specific requirement of very high rigidity and temperatureInformation provided by Bhansali
Flexural Yield Strength	80.4 MPa @Thickness 6.40 mm	11700 psi @Thickness 0.252 in	5 mm/min; ASTM D790
Bhansali Engineering Abstron IM14GL ABS Injection Molding Grade Super High Rigidity, Medium Impact, High Chemical ResistanceInformation provided by Bhansali