Samyang Tribit® 1501N PBT, Flame Retardancy
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Flame Retardant |
| Manufacturer | Samyang |
| Trade Name | Tribit® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Tribit® 1501N PBT, Flame Retardancy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Crystallization is fast, formability is excellent and thermal resistance, chemical resistance, electrical properties and abrasion resistance are excellent.1501N is a V-2 flame retardancy grade.Applications: Connectors (insulation characteristics)Information provided by Samyang.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 |
| Water Absorption | 0.080 % | 0.080 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.012 cm/cm | 0.0020 - 0.012 in/in | ASTM D955 |
| Melt Flow | 60 g/10 min @Load 2.16 kg, Temperature 235 °C |
60 g/10 min @Load 4.76 lb, Temperature 455 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength | 53.9 MPa | 7820 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Flexural Yield Strength | 80.4 MPa | 11700 psi | ASTM D790 |
| Flexural Modulus | 2.26 GPa | 327 ksi | ASTM D790 |
| Izod Impact, Notched | 0.588 J/cm @Thickness 3.17 mm |
1.10 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 0.810 mm |
V-2 @Thickness 0.0319 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.2 | 3.2 | ASTM D150 |
| Dielectric Strength | 18.0 kV/mm | 457 kV/in | ASTM D149 |
| Dissipation Factor | 0.020 | 0.020 | ASTM D150 |
| Arc Resistance | 71 sec | 71 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Garland Manufacturing GAR-DUR® Ultra High Molecular Weight Polyethylene (UHMW-PE)
- Materion Beryllium Copper Alloy M25 Wire; HT (TH04) Temper; 1.3-2.0 mm Diameter (UNS C17300)
- Karina E 40/43-RG-PO Green Color Concentrate for PVC
- Teknor Apex APEX® 94-A0098A-70 Polyvinyl Chloride, Flexible
- A. Schulman POLYBATCH™ CE-505-E Concentrate Based In Polyethylene
- A. Schulman POLYFLAM™ CFP 4623 20% Calcium Filled Polypropylene
- DuPont Performance Polymers Zytel® 70G35NOX BK309 Nylon 66
- Abatron AboCoat 8709-3 A/B Carbon-Filled Electrically Conductive Epoxy Compound
- Bhansali Engineering Abstron IM-17A(DLW) ABS Injection Molding Grade
- Overview of materials for Polyetherimide (PEI)
Copyright © lookpolymers.com All Rights Reserved