Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 5.50 - 38.0 MPa | 798 - 5510 psi | Average value: 20.6 MPa Grade Count:8 |
Overview of materials for Polytetrafluoroethylene (PTFE), Glass Filled, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polytetrafluoroethylene (PTFE), Glass Filled, Molded". Each property range of values reported is minimum.. |
|||
Flexural Yield Strength | 5.50 MPa @Strain 0.200 % |
798 psi @Strain 0.200 % |
ASTM D790 |
Dalau Dalcon 006 75% Virgin PTFE, 25% Glass Fiber Applications & Industries:General: 25% Glass fibre is the most widely used filler. It improves the creep resistance, compressive strength, rigidity, and wear of PTFE, both at low & high temperatures.. |
|||
Flexural Yield Strength | 5.50 MPa @Strain 0.200 % |
798 psi @Strain 0.200 % |
ASTM D790 |
Dalau Dalcon 025 75% Virgin PTFE, 25% Glass Fiber, Blue Applications & Industries: General: 25% Glass fibre is the most widely used filler. It improves the creep resistance, compressive strength, rigidity, and wear of PTFE, both at low & high temperature.. |
|||
Flexural Yield Strength | 5.50 MPa @Strain 0.200 % |
798 psi @Strain 0.200 % |
ASTM D790 |
Dalau Dalcon 006 75% Virgin PTFE, 25% Glass Fiber Applications & Industries:General: 25% Glass fibre is the most widely used filler. It improves the creep resistance, compressive strength, rigidity, and wear of PTFE, both at low & high temperatures.. |
|||
Flexural Yield Strength | 5.50 MPa @Strain 0.200 % |
798 psi @Strain 0.200 % |
ASTM D790 |
Dalau Dalcon 025 75% Virgin PTFE, 25% Glass Fiber, Blue Applications & Industries: General: 25% Glass fibre is the most widely used filler. It improves the creep resistance, compressive strength, rigidity, and wear of PTFE, both at low & high temperature.. |