Polymer Property : Flexural Yield Strength = 126 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	126 MPa	18300 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP FARADEX DX92079 PC (Europe-Africa-Middle East) LNP* Faradex* DX92079 is a compound based on Polycarbonate resin containing Glass Fiber, Glass Bead, Stainless Steel Fiber. Added features of this material include: EMI/RFI Shielding, Mold Release...
Flexural Yield Strength	126 - 317 MPa	18300 - 46000 psi	Average value: 249 MPa Grade Count:11
Overview of materials for Polyphenylene Sulfide (PPS) with 40% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 40% Carbon Fiber Filler". Specific grades with carbon fiber content bet..
Flexural Yield Strength	126 MPa	18300 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® VX5011 PBT (Europe-Africa-Middle East) VALOX VX5011 is a 10% glass fibre reinforced PBT+PC blend with low warpage characteristics.
Flexural Yield Strength	126 MPa	18300 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL NH5020 PPE+PS Noryl* NH5020 Resin is an unreinforced blend of Polyphenylene Ether(PPE) + Polystyrenre resin. The material offers a good balance of heat, flow, hydrolytic stability, and non-halogenated flame reta..
Flexural Yield Strength	126 MPa	18300 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL NH5020 PPE+PS (Asia Pacific) Noryl* NH5020 Resin is an unreinforced blend of Polyphenylene Ether(PPE) + Polystyrenre resin. The material offers a good balance of heat, flow, hydrolytic stability, and non-halogenated flame reta..
Flexural Yield Strength	126 MPa	18300 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL NH5020 PPE+PS (Europe-Africa-Middle East) Noryl* NH5020 Resin is an unreinforced blend of Polyphenylene Ether(PPE) + Polystyrenre resin. The material offers a good balance of heat, flow, hydrolytic stability, and non-halogenated flame reta..
Flexural Yield Strength	126 MPa	18300 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® SHF4930 PBT Super high flow FR PBT grade with 15% Glass reinforced
Flexural Yield Strength	126 MPa	18200 psi	ASTM D790
Cheng Yu Plastic FV30710 POM, 10% Mineral Reinforced
Flexural Yield Strength	126 MPa	18300 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP DFP32 PC LNP* LUBRICOMP* DFP32 is a compound based on Polycarbonate resin containing 10% Glass Fiber, 15% PTFE/Silicone. Added feature of this material is: Wear Resistant.
Flexural Yield Strength	126 MPa	18300 psi
Phenolic 35%, Carbon fabric 65% Phenolic - Monsanto "SC 1008". Carbon fabric - "VCA"
Flexural Yield Strength	126 MPa	18300 psi	DIN 53452; ASTM D790
Kolon Kopa® KN153G15 Nylon 6 Resin KOPA is widely used in the automobile and industrial parts.General KOPA N-6 Features: Good mechanical properties, Extreme toughness, Outstanding self-lubrication and abrasion resistance, Excellent c..
Flexural Yield Strength	126 MPa	18300 psi	ASTM D790-70
Budd Hi-Flex® SMC (discontinued **) Parts requiring high strength and dimensional stability, excellent surface smoothness without sink marks; parts to be painted requiring an automotive-type finish.Data provided by the manufacturer.