Polymer Property : Flexural Yield Strength = 12.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	12.0 MPa	1740 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP HX00059 PA11 (Europe-Africa-Middle East) LNP * Lubricomp * HX00059 is a compound based on PA 11 resin, containing a Proprietary Lubricant. Added features include: Internally Lubricated.
Flexural Yield Strength	12.0 MPa	1740 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP YL003 Polyester Elastomer (Europe-Africa-Middle East) LNP* LUBRICOMP* YL003 is a compound based on Polyester Elastomer containing PTFE. Added features include; Internally Lubricated.
Flexural Yield Strength	12.0 MPa	1740 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP YI001 Polyester Elastomer (Europe-Africa-Middle East) LNP* LUBRICOMP* YI001 is a compound based on Polyester Elastomer containing Silicone. Added features include; Internally Lubricated.
Flexural Yield Strength	12.0 - 85.0 MPa	1740 - 12300 psi	Average value: 35.7 MPa Grade Count:23
Overview of materials for Polypropylene with 10% Calcium Carbonate (CaCO3) Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 10% Calcium Carbonate (CaCO3) Filler". Specific grades with primary filler content be..