Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Yield, TD | 29.0 MPa @Temperature 23.0 °C |
4210 psi @Temperature 73.4 °F |
ASTM D638 |
Mapal Plastics Maplon Type 3G Polypropylene Sheet Maplon type “3G†is a single layer highly polished clear sheets, with anti-blocking properties.Main advantages: High clarity and low haze, Easy to convert due to reduced blocking, High dur.. |
|||
Film Tensile Strength at Yield, TD | 29.0 MPa @Temperature 23.0 °C |
4210 psi @Temperature 73.4 °F |
ASTM D638 |
Mapal Plastics Maplon Type D Polypropylene Sheet Main advantages: High clarity and medium haze, High durability, Water and chemical resistance, High heat resistance, Unlimited flex life of integral hinge, Easy to convertMain disadvantages: Low scr.. |
|||
Film Tensile Strength at Yield, TD | 29.0 MPa | 4210 psi | ISO 1184 |
SIDPEC EGYPTENE® HD 5301 FB HDPE Film Applications:Strong thin filmCarrier bagGrocery sacksFilm properties were measured on 15 micron film extruded at a blow up ratio of 5:1, 8D neck height.Information provided by Interchim s.r.l., offi.. |
|||
Film Tensile Strength at Yield, TD | 29.0 MPa | 4210 psi | ISO 527-3 |
Total PPH 4026 Polypropylene Homopolymer, Film Polypropylene PPH 4026 is a homopolymer polypropylene with a Melt Flow index of 3 g/10 min for the cast extrusion of films with outstanding stiffness and heat resistance.Polypropylene PPH 4026 is in.. |
|||
Film Tensile Strength at Yield, TD | 29.0 MPa | 4210 psi | ASTM D882 |
Braskem HF 0147 HDPE Blown Film Extrusion Polyethylene 38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Grocery and T-shirt bags; merchandise bags; frozen-food bags. Information provided by Bras.. |