Polymer Property : Film Tensile Strength at Yield, TD = 29.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, TD	29.0 MPa @Temperature 23.0 Â°C	4210 psi @Temperature 73.4 Â°F	ASTM D638
Mapal Plastics Maplon Type 3G Polypropylene Sheet Maplon type â€œ3Gâ€ is a single layer highly polished clear sheets, with anti-blocking properties.Main advantages: High clarity and low haze, Easy to convert due to reduced blocking, High dur..
Film Tensile Strength at Yield, TD	29.0 MPa @Temperature 23.0 Â°C	4210 psi @Temperature 73.4 Â°F	ASTM D638
Mapal Plastics Maplon Type D Polypropylene Sheet Main advantages: High clarity and medium haze, High durability, Water and chemical resistance, High heat resistance, Unlimited flex life of integral hinge, Easy to convertMain disadvantages: Low scr..
Film Tensile Strength at Yield, TD	29.0 MPa	4210 psi	ISO 1184
SIDPEC EGYPTENEÂ® HD 5301 FB HDPE Film Applications:Strong thin filmCarrier bagGrocery sacksFilm properties were measured on 15 micron film extruded at a blow up ratio of 5:1, 8D neck height.Information provided by Interchim s.r.l., offi..
Film Tensile Strength at Yield, TD	29.0 MPa	4210 psi	ISO 527-3
Total PPH 4026 Polypropylene Homopolymer, Film Polypropylene PPH 4026 is a homopolymer polypropylene with a Melt Flow index of 3 g/10 min for the cast extrusion of films with outstanding stiffness and heat resistance.Polypropylene PPH 4026 is in..
Film Tensile Strength at Yield, TD	29.0 MPa	4200 psi	ASTM D882
ExxonMobil HDPE HTA 001HP2 High Density Polyethylene (HMW) Resin Product Description: HTA 001HP2 is a high molecular weight HDPE film grade providing very good processability on high output extruders. Films made from HTA 011HP2 exhibit excellent impact and toughn..
Film Tensile Strength at Yield, TD	29.0 MPa	4200 psi	ASTM D882
ExxonMobil HDPE HTA 002 High Density Polyethylene Resin Product Description: HTA 002 is a general purpose medium molecular weight HDPE grade, characterized by easy processability, especially in coextrusion and blending with other polyolefins. HTA 002 can..
Film Tensile Strength at Yield, TD	29.0 MPa	4210 psi	ASTM D882
Braskem HF 0147 HDPE Blown Film Extrusion Polyethylene 38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Grocery and T-shirt bags; merchandise bags; frozen-food bags. Information provided by Bras..