Polymer Property : Shear Modulus = 69.0 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Shear Modulus	69.0 GPa @Temperature 593 Â°C	10000 ksi @Temperature 1100 Â°F
Haynes R-41 alloy, 0.635 mm thick sheet, solution heat treated at 1079Â°C, water quenched, 30 minutes at 1066Â°C, aged 16 hours at 760Â°C (1400Â°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Shear Modulus	69.0 GPa @Temperature 593 Â°C	10000 ksi @Temperature 1100 Â°F
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079Â°C, water quenched, 30 minutes at 1066Â°C, aged 16 hours at 760Â°C (1400Â°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Shear Modulus	69.0 GPa @Temperature 593 Â°C	10000 ksi @Temperature 1100 Â°F
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079Â°C, water quenched, 30 minutes at 1066Â°C, air cooled, aged 16 hours at 760Â°C (1400Â°F) Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Shear Modulus	69.0 GPa	10000 ksi
Elgiloy® Co-Cr-Ni Alloy, Wire, 47% Cold Reduction (Coil Spring Range) 45-48% cold reduction is the normal coil spring range. The strength, shear modulus, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.Ge..
Shear Modulus	69.0 GPa	10000 ksi
HP Alloys Nitronic® 60 Austenitic Stainless, Level 1 Cold Worked Level 1 Cold Worked applies to tensile properties of 0.25 to 4 in. sizes; other properties are typical of this alloy.Nitronic 60 is truly an all purpose metal. This fully austenitic alloy was origin..
Shear Modulus	69.0 GPa	10000 ksi
HP Alloys Nitronic® 60 Austenitic Stainless, Level 2 Cold Worked Level 2 Cold Worked applies to tensile and hardness properties of 0.25 to 4 in. sizes; other properties are typical of this alloy.Nitronic 60 is truly an all purpose metal. This fully austenitic all..
Shear Modulus	69.0 GPa	10000 ksi
HP Alloys Nitronic® 60 Austenitic Stainless, Level 3 Cold Worked Level 3 Cold Worked applies to tensile properties of 0.25 to 2.4 in. sizes; other properties are typical of this alloy.Nitronic 60 is truly an all purpose metal. This fully austenitic alloy was orig..
Shear Modulus	69.0 GPa	10000 ksi
HP Alloys Nitronic® 60 Austenitic Stainless, Annealed Annealed applies to tensile and/or hardness; other properties are typical of this alloy.Nitronic 60 is truly an all purpose metal. This fully austenitic alloy was originally designed as a high tempe..
Shear Modulus	69.0 GPa	10000 ksi
HP Alloys Nitronic® 60 Austenitic Stainless, Level 4 Cold Worked Level 4 Cold Worked applies to tensile properties of 0.25 to 2 in. sizes; other properties are typical of this alloy.Nitronic 60 is truly an all purpose metal. This fully austenitic alloy was origin..
Shear Modulus	69.0 GPa	10000 ksi
HP Alloys Nitronic® 60 Austenitic Stainless, Level 5 Cold Worked Level 5 Cold Worked applies to tensile properties of 0.25 to 1.5 in. sizes; other properties are typical of this alloy.Nitronic 60 is truly an all purpose metal. This fully austenitic alloy was orig..