HP Alloys Nitronic® 60 Austenitic Stainless, Annealed

Category Metal , Ferrous Metal , Heat Resisting , Stainless Steel , T S20000 Series Stainless Steel
Manufacturer High Performance Alloys, Inc
Trade Name Nitronic®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF HP Alloys Nitronic® 60 Austenitic Stainless, Annealed.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Annealed applies to tensile and/or hardness; other properties are typical of this alloy.Nitronic 60 is truly an all purpose metal. This fully austenitic alloy was originally designed as a high temperature alloy for temperatures around 1800ºF. The oxidation resistance of Nitronic 60 is similar to Type 309 S.S., and far superior to Type 304S.S. The additions of silicon and manganese have given the alloy a matrix to inhibit wear, galling, and fretting even in the annealed condition. Higher strengths are attainable through cold working the material and is still fully austenitic after severe cold-working. This working does not enhance the anti-galling properties as is normal for carbon steels and some stainless steels. The benefit to the cold or hot work put into the material is added strength and hardness. The chromium and nickel additions give it comparable corrosion to 304 and 316 stainless steels, while having approximately twice the yield strength. The high mechanical strength in annealed parts permits use of reduced cross sections for weight and cost reductions.Data provided by High Performance Alloys, Inc.
Physical Properties Metric English Comments
Density 7.62 g/cc
0.275 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 210
210
Estimated from Rockwell B
Hardness, Knoop 245
245
Estimated from Rockwell B
Hardness, Rockwell A 58
58
Estimated from Rockwell B
Hardness, Rockwell B 95
95
Hardness, Vickers 215
215
Estimated from Rockwell B
Tensile Strength, Ultimate 710 MPa
103000 psi
Tensile Strength, Yield 414 MPa

@Strain 0.200 %
60000 psi

@Strain 0.200 %
Elongation at Break 64 %
64 %
Reduction of Area 74 %
74 %
Modulus of Elasticity 179 GPa
26000 ksi
In Tension
Poissons Ratio 0.30
0.30
Calculated
Shear Modulus 69.0 GPa
10000 ksi
Thermal Properties Metric English Comments
CTE, linear 15.8 µm/m-°C

@Temperature 20.0 - 95.0 °C
8.78 µin/in-°F

@Temperature 68.0 - 203 °F
Component Elements Properties Metric English Comments
Chromium, Cr 17 %
17 %
Iron, Fe 62 %
62 %
As remainder
Manganese, Mn 8.0 %
8.0 %
Nickel, Ni 8.5 %
8.5 %
Nitrogen, N 0.14 %
0.14 %
Silicon, Si 4.0 %
4.0 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.000130 ohm-cm
0.000130 ohm-cm