Polymer Property : Shear Modulus = 11700 ksi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Shear Modulus | 81.0 GPa @Temperature 149 °C |
11700 ksi @Temperature 300 °F |
|
| Haynes R-41 alloy, 0.635 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
| Shear Modulus | 81.0 GPa @Temperature 149 °C |
11700 ksi @Temperature 300 °F |
|
| Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
| Shear Modulus | 81.0 GPa @Temperature 149 °C |
11700 ksi @Temperature 300 °F |
|
| Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F) Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
| Shear Modulus | 80.8 GPa | 11700 ksi | Calculated |
| CeramTec MZ 111 HIP Zirconia, ZrO2-Y2O3 MZ 111 HIP is a yttria-stabilized tetragonal zirconia ceramic. |
|||
| Shear Modulus | 80.8 GPa | 11700 ksi | Calculated |
| CeramTec MZ 111 Zirconia, ZrO2-Y2O3 MZ 111 is a yttria-stabilized tetragonal zirconia used in dental applications. |
|||
| Shear Modulus | 80.8 GPa | 11700 ksi | Calculated |
| CeramTec MZ 429 Zirconia, ZrO2-Y2O3 MZ 429 is a yttria-stabilized zirconia ceramic. |
|||
| Shear Modulus | 80.8 GPa | 11700 ksi | Calculated |
| CeramTec ZN 40 Zirconia, ZrO2-MgO ZN 40 is a zirconium oxide ceramic with an excellent surface finish and a higher strength than aluminum oxide. Its good crack resistance and anti-friction properties, combined with steel-like therma.. |
|||
| Shear Modulus | 80.7 GPa | 11700 ksi | |
| Crucible Steel 420 and 420F Chromium Steel Crucible 416 Plus is a hardenable chromium steel which is the general purpose cutlery grade. This grade is magnetic in all conditions. Information provided by Crucible Specialty Metals. |
|||
| Shear Modulus | 81.0 GPa | 11700 ksi | |
| ATI Allegheny Ludlum AL 200™ Nickel Alloy, UNS N02200 Ferromagnetic. Allegheny Ludlum AL 200 alloy is wrought commercially pure nickel. This alloy provides highly ductile mechanical properties across a wide temperature range. Either alloy provides c.. |
|||
| Shear Modulus | 81.0 GPa | 11700 ksi | |
| ATI Allegheny Ludlum AL 201™ Nickel Alloy, UNS N02201 Ferromagnetic. Allegheny Ludlum AL 201 alloy is wrought commercially pure nickel. This alloy provides highly ductile mechanical properties across a wide temperature range. Either alloy provides c.. |
|||