Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Modulus | <= 0.000700 GPa | <= 0.102 ksi | |
Arlon 0.008" (0.2032 mm) Primerless Thermabond® Uncured Silicone (99990A008) 0.008 in., ±0.001 (0.2 mm, ±0.03) uncured silicone on 0.003 in. (0.08 mm) nominal PTFE coated fiberglass; 0.001 in. (0.03 mm) FEP interleave; overall thickness 0.008 in ±0.001(0.2 mm ± 0.03). T.. |
|||
Shear Modulus | <= 0.000700 GPa | <= 0.102 ksi | |
Arlon 0.008" (0.2032 mm) Thermabond® Uncured Silicone (99510N008) 0.008 in., ±0.001 (0.2 mm, ±0.03) uncured silicone on 0.003 in. (0.08 mm) nominal PTFE coated fiberglass; 0.001 in. (0.03 mm) FEP interleave; overall thickness 0.008 in ±0.001(0.2 mm ± 0.03). T.. |
|||
Shear Modulus | <= 0.000700 GPa | <= 0.102 ksi | |
Arlon 0.015" (0.381 mm) Primerless Thermabond® Uncured Silicone (99990A015) 0.015 in., ±0.001 (0.38 mm, ±0.038) uncured silicone on 0.003 in. (0.08 mm) nominal PTFE coated fiberglass; 0.001 in. (0.03 mm) FEP interleave; overall thickness 0.015 in ±0.001(0.38 mm ± 0.038).. |
|||
Shear Modulus | <= 0.000700 GPa | <= 0.102 ksi | |
Arlon 0.015" (0.381 mm) Thermabond® Uncured Silicone (99510N015) 0.015 in., ±0.001 (0.38 mm, ±0.038) uncured silicone on 0.003 in. (0.08 mm) nominal PTFE coated fiberglass; 0.001 in. (0.03 mm) FEP interleave; overall thickness 0.015 in ±0.001(0.38 mm ± 0.038).. |