Polymer Property : Tensile Modulus = 631 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	4.35 GPa	631 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics Cycoloy® CM6240 PC+ABS (Asia Pacific) CYCOLOY CM6240 resin is a flame retardant PC/ABS blend featuring balanced properties of high modulus, good flow and ductility. It is of Br- & Cl-free flame retardant systems intended to meet thin wa..
Tensile Modulus	4.35 GPa	631 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DFL32 PC LNP LUBRICOMP* DFL32 is a compound based on Polycarbonate resin containing 10% Glass Fiber and 15% PTFE. Added features of this material include: Internally Lubricated.
Tensile Modulus	4.35 GPa	631 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DFL32XXC PC LNP LUBRICOMP* DFL32XXC is a compound based on Polycarbonate resin containing 10% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated.
Tensile Modulus	4.35 GPa	631 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP DFL42 PC LNP* Lubricomp* DFL-4042 a compound based on Polycarbonate resin containing 10% Glass Fiber, 20% PTFE. Added features include: Internally Lubricated.
Tensile Modulus	4.35 GPa	631 ksi	ISO 527 Type 1A
Solvay TECHNYLÂ® C 52G1 V25 Grey R7035 (XC 1329/A) PA6, Conditioned Description: Polyamide 6, Glass-filled, glow-wire modified, color stabilized, lubricated for injection molding.Available in: Asia Pacific, Europe, Latin America and North America Product Application..
Tensile Modulus	4.35 GPa	631 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics ValoxÂ® SHF4910 PBT (Europe-Africa-Middle East) 6.5% glass reinforced, Super High Flow, flame retardant PBT.
Tensile Modulus	4.35 GPa	631 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL GFN1 PPE+PS PPE+PS blend. 10% Glass reinforced. NSF 61 listing in several colors (restrictions apply). FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Sui..
Tensile Modulus	4.35 GPa @Temperature 75.0 °C	631 ksi @Temperature 167 °F	Dynamic; ISO 11403-1 -2
DuPont Performance Polymers Crastin® LW9320 NC010 PBT+SAN (Unverified Data**) 20% Glass Reinforced Polybutylene Terephthalate Blend with Low Warpage Characteristics Crastin LW9320 NC010 is a 20% glass fiber reinforced polybutylene terephthalate blend for injection molding. I..