SABIC Innovative Plastics LNP LUBRICOMP DFL32 PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP DFL32 PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* DFL32 is a compound based on Polycarbonate resin containing 10% Glass Fiber and 15% PTFE. Added features of this material include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
ASTM D792
Moisture Absorption 0.110 %
0.110 %
50% RH, 24 hrs; ASTM D570
0.170 %
0.170 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0020 cm/cm

@Time 86400 sec
0.0020 in/in

@Time 24.0 hour
ASTM D955
0.0023 cm/cm

@Time 86400 sec
0.0023 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0067 cm/cm

@Time 86400 sec
0.0067 in/in

@Time 24.0 hour
ISO 294
0.0070 cm/cm

@Time 86400 sec
0.0070 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 71.0 MPa
10300 psi
ISO 527
73.0 MPa
10600 psi
ASTM D638
Elongation at Break 2.8 %
2.8 %
ISO 527
3.1 %
3.1 %
ASTM D638
Tensile Modulus 4.28 GPa
621 ksi
1 mm/min; ISO 527
4.35 GPa
631 ksi
50 mm/min; ASTM D638
Flexural Strength 114 MPa
16500 psi
ISO 178
123 MPa
17800 psi
ASTM D790
Flexural Modulus 4.17 GPa
605 ksi
ISO 178
4.35 GPa
631 ksi
ASTM D790
Izod Impact, Notched 0.900 J/cm
1.69 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.34 J/cm
10.0 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 34.0 kJ/m²
16.2 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 11.0 J
8.11 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 4.00 J
2.95 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 140 °C
284 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
141 °C

@Thickness 3.20 mm
286 °F

@Thickness 0.126 in
unannealed; ASTM D648