| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Modulus | 193 GPa | 28000 ksi | |
| PSM Industries PolyAlloys MIM-17-4 PH Heat Treated Stainless Steel Information Provided by PolyAlloys, a division of PSM Industries |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 301 Austenitic Stainless Steel, 1/2 Hardened Type 301 is a chromium-nickel stainless steel that provides high strength and good ductility with chromium and nickel contents lowered to increase the work hardening range. This permits higher tens.. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 301 Austenitic Stainless Steel, 1/4 Hardened Type 301 is a chromium-nickel stainless steel that provides high strength and good ductility with chromium and nickel contents lowered to increase the work hardening range. This permits higher tens.. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 301 Austenitic Stainless Steel, 1/8 Hardened Type 301 is a chromium-nickel stainless steel that provides high strength and good ductility with chromium and nickel contents lowered to increase the work hardening range. This permits higher tens.. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 301 Austenitic Stainless Steel, 3/4 Hardened Type 301 is a chromium-nickel stainless steel that provides high strength and good ductility with chromium and nickel contents lowered to increase the work hardening range. This permits higher tens.. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 301 Austenitic Stainless Steel, Annealed Type 301 is a chromium-nickel stainless steel that provides high strength and good ductility with chromium and nickel contents lowered to increase the work hardening range. This permits higher tens.. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 301 Austenitic Stainless Steel, Full Hardened Type 301 is a chromium-nickel stainless steel that provides high strength and good ductility with chromium and nickel contents lowered to increase the work hardening range. This permits higher tens.. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 302 Austenitic Stainless Steel, 1/2 Hardened Types 302 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa.. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 302 Austenitic Stainless Steel, 1/8 Hardened Types 302 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa.. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 302 Austenitic Stainless Steel, Annealed Types 302 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa.. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 302 Austenitic Stainless Steel, Full Hardened Types 302 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa.. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 304 Austenitic Stainless Steel, 1/2 Hardened Types 304 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa.. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 304L Austenitic Stainless Steel, Annealed Type 304L is a very common variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled. Lower carbon 304L minimizes chromium ca.. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 305 Austenitic Stainless Steel, 1/4 Hardened Type 305 is a chromium nickel stainless steel that can be spun and deep drawn more easily due to an increased nickel content that decreases work hardening. It is nonmagnetic under most conditions. .. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 316 Austenitic Stainless Steel, 1/2 Hardened The Mo addition increases general corrosion resistance to pitting from chloride ion solutions, and provides increased strength at elevated temperatures. Properties are similar to those of Type 304 .. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 316 Austenitic Stainless Steel, 1/4 Hardened The Mo addition increases general corrosion resistance to pitting from chloride ion solutions, and provides increased strength at elevated temperatures. Properties are similar to those of Type 304 .. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 316 Austenitic Stainless Steel, 1/8 Hardened The Mo addition increases general corrosion resistance to pitting from chloride ion solutions, and provides increased strength at elevated temperatures. Properties are similar to those of Type 304 .. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 316 Austenitic Stainless Steel, 3/4 Hardened The Mo addition increases general corrosion resistance to pitting from chloride ion solutions, and provides increased strength at elevated temperatures. Properties are similar to those of Type 304 .. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 316 Austenitic Stainless Steel, Annealed The Mo addition increases general corrosion resistance to pitting from chloride ion solutions, and provides increased strength at elevated temperatures. Properties are similar to those of Type 304 .. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 316L Austenitic Stainless Steel, 1/4 Hardened Type 316L is an extra-low carbon version of Type 316 that minimizes carbide precipitation. Typical uses include exhaust manifolds, furnace parts, heat exchangers, jet engine parts, pharmaceutical a.. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 316L Austenitic Stainless Steel, 3/4 Hardened Type 316L is an extra-low carbon version of Type 316 that minimizes carbide precipitation. Typical uses include exhaust manifolds, furnace parts, heat exchangers, jet engine parts, pharmaceutical a.. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 316L Austenitic Stainless Steel, Full Hardened Type 316L is an extra-low carbon version of Type 316 that minimizes carbide precipitation. Typical uses include exhaust manifolds, furnace parts, heat exchangers, jet engine parts, pharmaceutical a.. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 304 Austenitic Stainless Steel, 1/4 Hardened Types 304 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa.. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 304 Austenitic Stainless Steel, 1/8 Hardened Types 304 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa.. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 304 Austenitic Stainless Steel, Annealed Types 304 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa.. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 304 Austenitic Stainless Steel, Full Hardened Types 304 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa.. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 304L Austenitic Stainless Steel, 1/2 Hardened Type 304L is a very common variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled. Lower carbon 304L minimizes chromium ca.. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | |
| Eagle Brass 304L Austenitic Stainless Steel, 1/4 Hardened Type 304L is a very common variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled. Lower carbon 304L minimizes chromium ca.. |
|||
| Tensile Modulus | 193 GPa @Temperature 23.0 °C |
28000 ksi @Temperature 73.4 °F |
|
| Carpenter 20Cb-3® Stainless Steel Data provided by Carpenter Technology Corporation.20Cb-3® is an austenitic stainless steel possessing excellent resistance to hot sulfuric acid and many other aggressive environments which would re.. |
|||
| Tensile Modulus | 193 GPa | 28000 ksi | filament |
| 3M Nextel™ CF-40 Woven Fabric 550 Information provided by 3M |
|||