Polymer Property : Tensile Modulus = 20.3 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	>= 0.140 GPa	>= 20.3 ksi	2% sec, TD; ASTM D882
NIZHNEKAMSKNEFTEKHIM PE 4117N (18401) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
Tensile Modulus	>= 0.140 GPa	>= 20.3 ksi	2% sec, TD; ASTM D882
NIZHNEKAMSKNEFTEKHIM PE 4118N (18401) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
Tensile Modulus	>= 0.140 GPa	>= 20.3 ksi	2% sec, TD; ASTM D882
NIZHNEKAMSKNEFTEKHIM PE 5117N (18601) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
Tensile Modulus	>= 0.140 GPa	>= 20.3 ksi	2% sec, TD; ASTM D882
NIZHNEKAMSKNEFTEKHIM PE 5117P (18602) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
Tensile Modulus	>= 0.140 GPa	>= 20.3 ksi	2% sec, TD; ASTM D882
NIZHNEKAMSKNEFTEKHIM PE 5118N (18601) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
Tensile Modulus	>= 0.140 GPa	>= 20.3 ksi	2% sec, TD; ASTM D882
NIZHNEKAMSKNEFTEKHIM PE 5118P (18602) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
Tensile Modulus	>= 0.140 GPa	>= 20.3 ksi	2% sec, TD; ASTM D882
NIZHNEKAMSKNEFTEKHIM PE 4117P (18402) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
Tensile Modulus	>= 0.140 GPa	>= 20.3 ksi	2% sec, TD; ASTM D882
NIZHNEKAMSKNEFTEKHIM PE 4118P (18402) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
Tensile Modulus	>= 0.140 GPa	>= 20.3 ksi	in the plane; ISO 527 1-2
3A Composites Core Materials AIREXÂ® C70.200 Universal Structural Foam AIREXÂ® C70 is a closed cell, crosslinked polymer foam that combines excellent stiffness and strength to weight ratios with superior toughness. It is non-friable, contains no CFCâ€™s, has negli..
Tensile Modulus	0.140 GPa	20.3 ksi
Kuraray HYBRARÂ® PH4 Polypropylene Blend Description: HYBRARÂ® is another in the series of new high performance thermoplastic rubbers developed by KURARAY using their unique isoprene technology. HYBRARÂ® is a special thermoplastic rubb..
Tensile Modulus	0.140 GPa	20.3 ksi
Kuraray HYBRARÂ® PH7 Polypropylene Blend Description: HYBRARÂ® is another in the series of new high performance thermoplastic rubbers developed by KURARAY using their unique isoprene technology. HYBRARÂ® is a special thermoplastic rubb..
Tensile Modulus	0.140 GPa	20.3 ksi	Bending Modulus; ASTM D790
UBE UMERIT 500F Metallocene LLDPE Description: UBE Super Polyethylene Umerit® is an ethylene-olefin copolymer made by UBE using the metallocene catalytic method. The metallocene catalytic method results in superior physical propert..
Tensile Modulus	0.140 GPa	20.3 ksi	ISO 527-1/-2
DuPont Performance Polymers Hytrel® HTR8068 Polyester Elastomer TPC-ET (Unverified Data**) 44 Shore D Flame Retardant Polyester Elastomer Developed for Extrusion and Injection Molding Information provided by DuPont Performance Polymers
Tensile Modulus	0.140 GPa	20.3 ksi	1 mm/min
Arkema Group Evatane® 1003 VL 2 Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Anti-UV stabilized grade. Applications Thermal and colorless agricultural film to 180 at 200 µ for greenhouse coverage.ISO data provided by the ..
Tensile Modulus	0.140 GPa	20.3 ksi	1 mm/min
Arkema Group Evatane® 1005 VN 2 Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process.Applications Grade for transparent and resistant film production. Examples: curtain stretch, coextrusion, stretch hood.ISO data provided by the ma..
Tensile Modulus	0.140 GPa	20.3 ksi	1 mm/min
Arkema Group Evatane® 1020 VB 2 Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Applications Grade for transparent, resistant films, sealable at low temperature. Examples: laminates.ISO data provided by the manufacturer, Arke..
Tensile Modulus	0.140 GPa	20.3 ksi	1 mm/min
Arkema Group Evatane® 1005 VG 2 Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Applications Grade for strength films, sealable at low temperature with some hot tack. Examples: rigid bags, deep-freeze packaging, laminates, co..
Tensile Modulus	0.140 GPa	20.3 ksi	1 mm/min
Arkema Group Evatane® 1006 VL 2E Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Anti-UV stabilized grade. Applications Thermal and colorless agricultural film to 200 at 210 µm for greenhouse coverage.ISO data provided by the..
Tensile Modulus	0.140 GPa	20.3 ksi	1 mm/min
Arkema Group Evatane® 1020 VG 2 Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Applications Grade for resistant films, sealable at low temperature with some hot tack. Examples: bags, deep-freeze packaging, laminates, coextru..
Tensile Modulus	0.140 GPa	20.3 ksi	ISO 527-1/-2
DSM Arnitel® CM551 TPC-ES Heat Resistant Copolyester