Polymer Property : Tensile Modulus = 141 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	0.970 GPa	141 ksi	1 mm/min; ISO 527
BASF Capron® 8202 NL Nylon 6 (Conditioned) (discontinued **) Information provided by BASF Corporation.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.
Tensile Modulus	0.970 GPa	141 ksi	1mm/min; ISO 527
BASF Ultramid® 8202 HS BK-102 PA6 (Conditioned) Ultramid 8202 HS BK-102 is an unfilled, heat stabilized, pigmented black, low viscosity, general purpose injection molding PA6 exhibiting excellent fluidity for filling thin sections. It possesses ..
Tensile Modulus	0.970 GPa	141 ksi	1mm/min; ISO 527
BASF Ultramid® 8202 HS PA6 (Conditioned) Ultramid 8202 HS is a heat stabilized, low viscosity, general purpose nylon 6 injection molding homopolymer. It possesses the combination of strength and toughness and has excellent chemical and ab..
Tensile Modulus	0.970 GPa	141 ksi	1mm/min; ISO 527
BASF Ultramid® 8202 PA6 (Conditioned) Ultramid 8202 is a low viscosity, general purpose polyamide 6 injection molding homopolymer exhibiting excellent melt fluidity for filling thin sections. It is also available in heat stabilized (Ult..
Tensile Modulus	0.970 GPa @Temperature 120 °C	141 ksi @Temperature 248 °F	ISO Data
BASF Ultramid® 8260 40% Mineral Filled PA6 (Dry) Ultramid 8260 is a 40% mineral reinforced PA6 injection molding compound. It possesses high stiffness, dimensional stability and heat resistance combined with excellent processability including low..
Tensile Modulus	0.970 GPa @Temperature 120 °C	141 ksi @Temperature 248 °F	ISO Data
BASF Ultramid® 8260 HS BK-102 40% Mineral Filled PA6 (Dry) Ultramid 8260 HS BK-102 is a heat stabilized, pigmented black, 40% mineral reinforced PA6 injection molding resin. It possesses high stiffness, dimensional stability and heat resistance combined wi..