Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 10.44 GPa | 1514 ksi | ISO 527 |
Nilit FRIANYL C73 TFGV1530 Nylon 6.6/6 for injection molding, 15% PTFE lubricated, 30% glass fiber reinforced Nylon 6.6/6 for injection molding, medium viscosity.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Tensile Modulus | 10.44 GPa | 1514 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RFL36U PA 66 LNP* LUBRICOMP* RFL36U is a compound based on Nylon 66 resin containing 15% PTFE, 30% Glass Fiber. Added features of this grade include: Wear Resistant, UV Stabilized. |
|||
Tensile Modulus | 10.44 GPa | 1514 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP WF006H PBT LNP* THERMOCOMP* WF006H is a compound based on PBT resin containing 30% Glass Fiber. Added feature of this grade is: Healthcare. |
|||
Tensile Modulus | 10.44 GPa | 1514 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP VERTON MV00AS PP (Asia Pacific) LNP VERTON* MV00AS is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled. |
|||
Tensile Modulus | 10.44 GPa | 1514 ksi | 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Verton MX03017 PP (Europe-Africa-Middle East) LNP* VERTON* MX03017 is a compound based on Polypropylene resin containing Glass Fiber, Long Glass Fiber. Added features of this material include: Chemically Coupled.This data was supplied by SABIC.. |
|||
Tensile Modulus | 10.44 GPa | 1514 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP WF006H PBT (Asia Pacific) LNP* Thermocomp* WF006H is a compound based on Polybutylene Terephalate resin containing Glass Fiber. |
|||
Tensile Modulus | 10.44 GPa | 1514 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP VERTON MV00ASXP PP (Europe-Africa-Middle East) LNP VERTON* MV00AS is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled. |
|||
Tensile Modulus | 10.44 GPa | 1514 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Verton RV008ESV_GY7E072 PA 66 Preliminary data for 40% long glass fiber filled, single color pellet gray, PA66This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Modulus | 10.44 GPa | 1514 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP VERTON MV00AS PP LNP VERTON* MV00AS is a compound based on Polypropylene resin containing 50% Long Glass Fiber. Added features of this material include: Chemically Coupled, Heat Stabilized, Structural. |
|||
Tensile Modulus | 10.44 GPa | 1514 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP VERTON MV00ASU PP LNP VERTON* MV00ASU is a compound based on Polypropylene resin containing 50% Long Glass Fiber. Added features of this material include: Chemically Coupled, Heat Stabilized, UV Stabilized, Structur.. |
|||
Tensile Modulus | 10.44 GPa | 1514 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP VERTON MV00ASU PP (Asia Pacific) LNP VERTON* MV00ASU is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled. |
|||
Tensile Modulus | 10.44 GPa | 1514 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP VERTON MV00ASU PP (Europe-Africa-Middle East) LNP VERTON* MV00ASU is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled. |