Polymer Property : Tensile Strength, Yield = 96000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	662 MPa @Temperature 82.2 °C	96000 psi @Temperature 180 °F	0° Direction, Wet; Vacuum/Oven Cured; ASTM D3039-95
Park Electrochemical Nelcote® E-765 Epoxy Prepreg, T300 3K PW Reinforced Nelcote® E-765 is a tough 250°F cure prepreg system designed to replace 350°F cure systems in aircraft structural applications. FAA-approved Design Allowable Databases are available upon request...
Tensile Strength, Yield	662 - 765 MPa	96000 - 111000 psi	0.2% offset
Eagle Brass 519 Phosphor Bronzes 6%, Spring Alloy C519 has 6% nominal tin producing higher mechanical strengths with a slight decrease in electrical conductivity when compared to C510 phosphor bronze. Often functionally interchangeable with C..
Tensile Strength, Yield	662 MPa @Strain 0.200 %, Temperature 705 °C	96000 psi @Strain 0.200 %, Temperature 1300 °F
Carpenter Thermo-Span® Fe-Co-Ni Superalloy Data provided by Carpenter Technology Corporation.Thermo-Span® alloy is a precipitation hardenable superalloy which exhibits a low coefficient of thermal expansion over a broad temperature range, h..
Tensile Strength, Yield	662 MPa @Strain 0.200 %, Temperature -73.0 °C	96000 psi @Strain 0.200 %, Temperature -99.4 °F
Carpenter Custom 450® Stainless Steel, Condition H1150 (Age Hardened 621°C) Data provided by Carpenter Technology Corporation.Custom 450® stainless is a martensitic age-hardenable stainless steel which exhibits very good corrosion resistance (similar to that of Stainless T..
Tensile Strength, Yield	662 MPa @Strain 0.200 %	96000 psi @Strain 0.200 %
Kennametal Stellite Stellite® 31 PM cast aged 8 hours at 802°C air cooled Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous we..