Polymer Property : Tensile Strength, Yield = 845 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	845 MPa @Strain 0.200 %	123000 psi @Strain 0.200 %
Haynes MultimetÂ® alloy, 6.15 mm hot-rolled bar, 15% cold reduction Recommended for use in applications involving high stress at temperatures up to 816Â°C (1500Â°F), and moderate stresses up to 1093Â°C (2000Â°F). Excellent oxidation resistance, good ductilit..
Tensile Strength, Yield	845 MPa @Strain 0.200 %	123000 psi @Strain 0.200 %
Haynes 242Â® alloy, bar and rings, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815Â°C, excellent low cycle fatigue properties, very good therm..
Tensile Strength, Yield	845 MPa @Strain 0.200 %	123000 psi @Strain 0.200 %
Haynes 625 alloy, plate after 1000 hours at 650Â°C (1200Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Tensile Strength, Yield	845 MPa	123000 psi	Hardened 1800°F, Tempered 900°F
ATI Allegheny Ludlum 410 Martensitic Stainless Steel Characteristics: superior wear resistance, hardenable, excellent corrosion resistance. Applications:cutlery, dental and surgical instruments, nozzles, valve parts, hardened steel ball and seats for..
Tensile Strength, Yield	845 MPa @Strain 0.200 %	123000 psi @Strain 0.200 %	typical
ATI Allegheny Ludlum Martensitic Stainless Steel Type 410, Hardened + 482°C Temper Allegheny Ludlum Type 410 is a hardenable straight-chromium stainless steel which combines superior wear resistance of high carbon alloys with the excellent corrosion resistance of chromium stainles..