Polymer Property : Tensile Strength, Yield = 76100 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Tensile Strength, Yield	525 MPa @Strain 0.200 %, Temperature 650 Â°C	76100 psi @Strain 0.200 %, Temperature 1200 Â°F
Haynes 214Â® alloy, hot rolled solution annealed plate 12.7 mm (1/2 in.) thick Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Yield	525 MPa @Strain 0.200 %	76100 psi @Strain 0.200 %
Haynes 230Â® alloy, 30% cold reduction, 1066Â°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149Â°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Tensile Strength, Yield	525 MPa @Strain 0.200 %	76100 psi @Strain 0.200 %
Haynes 230Â® alloy, 40% cold reduction, 1121Â°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149Â°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Tensile Strength, Yield	525 MPa	76100 psi
Haynes HastelloyÂ® W alloy, shielded metal arc welds, as-welded Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica..
Tensile Strength, Yield	525 MPa @Strain 0.200 %, Temperature 650 Â°C	76100 psi @Strain 0.200 %, Temperature 1200 Â°F
Haynes 263Â® alloy, cold rolled sheet, solution treated and aged Very good aged strength properties, excellent fabrication characteristics when annealed, excellent intermediate temperature tensile ductility, is not normally subject to strain age cracking, excelle..
Tensile Strength, Yield	525 MPa @Strain 0.200 %	76100 psi @Strain 0.200 %
Special Metals INCONELÂ® 625LCFÂ® Nickel Superalloy (UNS N06626) Annealed + 20% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 9.0. Other property values are typical of t..
Tensile Strength, Yield	525 MPa @Strain 0.200 %, Temperature 650 °C	76100 psi @Strain 0.200 %, Temperature 1200 °F
Haynes 242® alloy, hot rolled plate, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good thermal..