Polymer Property : Tensile Strength, Yield = 680 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	680 - 830 MPa	98600 - 120000 psi
Materion Beryllium Copper Alloy 10 Plate & Rolled Bar; HT (TH04) Temper; up to 76 mm Thickness (UNS C17500) Treatment required for max strength: 2 hrs @ 480Â°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials In..
Tensile Strength, Yield	680 - 830 MPa	98600 - 120000 psi
Materion Beryllium Copper Alloy 3 Plate & Rolled Bar; HT (TH04) Temper; up to 76 mm Thickness (UNS C17510) Treatment required for max strength: 2 hrs @ 480Â°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials In..
Tensile Strength, Yield	680 MPa @Strain 0.200 %	98600 psi @Strain 0.200 %
Haynes 214Â® alloy, sheet, 1000 hours exposure at 760Â°C (1400Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Yield	680 MPa @Strain 0.200 %, Temperature 650 Â°C	98600 psi @Strain 0.200 %, Temperature 1200 Â°F
Haynes 242Â® alloy, cold rolled sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815Â°C, excellent low cycle fatigue properties, very good therm..
Tensile Strength, Yield	680 MPa @Strain 0.200 %, Temperature 650 Â°C	98600 psi @Strain 0.200 %, Temperature 1200 Â°F	Precipitation Hardened prior to test
Special Metals NIMONICÂ® Alloy PE11 A nickel-iron-chromium alloy precipitation hardened by titanium and aluminum and solid-solution strengthened by an addition of molybdenum. It was developed as a high-strength sheet alloy for use at..
Tensile Strength, Yield	>= 680 MPa @Thickness >=8.00 mm	>= 98600 psi @Thickness >=0.315 in
ThyssenKrupp PAS 700 Structural Steel for Cold Forming This Material Specification applies to plates made of low carbon high strength steels with minimum yield strength values between 315 and 700 MPa1) in the thermo mechanically rolled delivery conditio..
Tensile Strength, Yield	680 - 830 MPa	98600 - 120000 psi
ArcelorMittal Complex Phase Steel 800 Very high strength steel, Hot Rolled Steel Available in the following: uncoated (HCT780C) and Extragal®/Galvannealed (HCT780C+Z)Description: The Complex Phase family of steels supplements ArcelorMittal's VHSS (very high strength steel) prod..