Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 27.9 MPa | 4050 psi | ASTM D638 |
Multibase Multi-Pro® 1012 C Polypropylene Calcium Carbonate Filler, 12% by weight.Forms:PelletsProcessing Methods:Injection MoldingInformation provided by Multibase |
|||
Tensile Strength, Yield | 27.9 MPa | 4050 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Plasticizer SC MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 27.9 MPa | 4050 psi | aged in air at 100ºC for 4 days |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Sundex 790 Plasticizer MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 27.9 MPa | 4050 psi | ASTM D638 |
IRPC Polimaxx Polene 2311NCX TA4 Polypropylene Compound CHARACTERISTICS: POLYPROPYLENE BLOCK COPOLYMER WITH 20% TALCUM REINFORCED, HIGH IMPACT STRENGTHAPPLICATIONS: INJECTION MOLDING FOR AUTOPARTS, ELECTRICAL APPLIANCES |
|||
Tensile Strength, Yield | 27.9 MPa | 4050 psi | ASTM D638 |
IRPC Polimaxx Polene 2311SCX TA4 Polypropylene Compound CHARACTERISTICS: POLYPROPYLENE BLOCK COPOLYMER WITH 20% TALCUM REINFORCED GOOD IMPACT STRENGTH, HIGH FLOWAPPLICATIONS: INJECTION MOLDING FOR AUTOPARTS, ELECTRICAL APPLIANCES |
|||
Tensile Strength, Yield | 27.9 MPa | 4050 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Plasticizer SC MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 27.9 MPa | 4050 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with TCP Plasticizer MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 27.9 MPa | 4050 psi | after 7 days at 100ºC |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 0.75 PHR Sulfur MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 27.9 MPa | 4050 psi | |
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 76A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
Tensile Strength, Yield | 27.9 MPa | 4050 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR N330 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 27.9 MPa | 4050 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR N990 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 27.9 MPa | 4050 psi | aged in air at 100ºC for 4 days |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Sundex 790 Plasticizer MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 27.9 MPa | 4050 psi | |
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 76A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
Tensile Strength, Yield | 27.9 MPa | 4050 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR N330 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 27.9 MPa | 4050 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR N990 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 27.9 MPa | 4050 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with TCP Plasticizer MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 27.9 MPa | 4050 psi | after 7 days at 100ºC |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 0.75 PHR Sulfur MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |