Polymer Property : Tensile Strength, Yield = 365 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	365 MPa @Temperature 21.1 °C	53000 psi @Temperature 70.0 °F	0° Direction, Dry; Vacuum/Oven Cured; ASTM D3039-95
Park Electrochemical Nelcote® E-765 Epoxy Prepreg, 120 E-Glass Reinforced Nelcote® E-765 is a tough 250°F cure prepreg system designed to replace 350°F cure systems in aircraft structural applications. FAA-approved Design Allowable Databases are available upon request...
Tensile Strength, Yield	365 MPa @Strain 0.200 %	52900 psi @Strain 0.200 %
Haynes HastelloyÂ® S alloy, weld metal, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Tensile Strength, Yield	365 MPa @Diameter 12.7 mm	52900 psi @Diameter 0.500 in
Kaiser 4026 T8 Rod & Bar This alloy is used when high strength with wear and/or galling resistance is required. It can eliminate hard-coat anodizing in some applications. Typical applications include air compressor pistons ..
Tensile Strength, Yield	365 MPa	53000 psi
Mueller Alloy 4850 Naval Brass - High Leaded (UNS C48500) Alloy noted for its machinability and resistance to wear, fatigue, galling and stress corrosion crackingApplications: The alloy is typically used for fastener, valve stems, screw machine products an..
Tensile Strength, Yield	365 MPa @Strain 0.200 %	52900 psi @Strain 0.200 %
Haynes 556Â® alloy, 0% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Yield	365 MPa @Strain 0.200 %	52900 psi @Strain 0.200 %
Haynes 556Â® alloy, 0% cold reduction, 1010Â°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Yield	365 MPa @Strain 0.200 %	52900 psi @Strain 0.200 %
Haynes 556Â® alloy, 0% cold reduction, 1065Â°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Yield	365 MPa @Strain 0.200 %	52900 psi @Strain 0.200 %
Haynes 625 alloy, 30% cold reduction, 1175Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Tensile Strength, Yield	365 MPa	52900 psi	Open Hole Tension, Hot/Wet
Hexcel® HexPly® M36 180°C (350°F) Curing Epoxy Matrix, Unidirectional Prepreg Laminate (M36/32%/135/HTA) Tenax HTA fiberInformation provided by HexCel
Tensile Strength, Yield	365 - 469 MPa	53000 - 68000 psi	0.2% offset
Eagle Brass 194 HSM® Copper, Hard High Strength Modified Copper Alloy C194 is a first generation high performance alloy used worldwide. C194 combines good electrical conductivity with high tensile strength, good solderability and pl..
Tensile Strength, Yield	365 - 434 MPa	53000 - 63000 psi	0.2% offset
Eagle Brass 220 Commercial Bronze, Hard CDA 220 is known for having very good corrosion resistance, great cold workability and good hot workability for drawing, blanking, coining, stamping, piercing and punching. Typical uses include plum..
Tensile Strength, Yield	365 MPa @Strain 0.200 %	52900 psi @Strain 0.200 %
Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GTAW short arc weld 1.1 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin..