Polymer Property : Tensile Strength, Yield = 2.70 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	2.70 MPa	392 psi	ISO 527
Polimeri Europa Greenflex® HN 70 Ethylene Vinyl Acetate Copolymer - Compounding Greenflex HN 70 is an ethylene vinyl acetate copolymer (EVA) for compounding applications. Greenflex HN 70 is a medium fluidity grade with high tack.Main Applications: Greenflex HN 70 is recommend..
Tensile Strength, Yield	2.70 MPa	392 psi	M100
3M Dyneon™ Aflas® FA-150E PTFE Fluoroelastomer (discontinued **) Data provided by the manufacturer, Dyneon LLC.Non-incorporated cure polymer, 57%F in polymer with 19% Medium Thermal Carbon Black (N990), 4% Triallyl Isocyanurate (TAIC), 1% Percadox™ 14, 1% Sodium..
Tensile Strength, Yield	2.70 - 6.50 MPa	392 - 943 psi	Average value: 4.82 MPa Grade Count:4
Overview of materials for Ethylene Vinyl Acetate Copolymer (EVA), Adhesive/Sealant Grade This property data is a summary of similar materials in the MatWeb database for the category "Ethylene Vinyl Acetate Copolymer (EVA), Adhesive/Sealant Grade". Each property range of values reported ..
Tensile Strength, Yield	2.70 MPa	391 psi	at 200%, post cured- 2 hours at 177Â°C; ASTM D412
Multibase C6-540 Dow-Corning Class VI Elastomer Information provided by Multibase
Tensile Strength, Yield	2.70 MPa	391 psi	AVG Stress at Elongation M100; ASTM D412 Method A
Seals Eastern 7284 Butyl and Halobutyl Rubber Chlorobutyl; High damping; Non-conductiveInformation provided by Seals Eastern, Inc.
Tensile Strength, Yield	2.70 MPa @Strain 100 %	392 psi @Strain 100 %
Daikin DAI-EL G-558 Fluoroelastomer Terpolymer, Bisphenol Curable Grade, 69% Fluorine Content Offers minimal compression set and excellent sealing. The terpolymer type is able to withstand polarized solvents to realize a wide range of application.Features: Low gasoline permeability and good..
Tensile Strength, Yield	2.70 MPa	392 psi
ACC MM913 Condensation Cure 2-Part Molding Rubber Part of the Amber Chemical Group. Data provided by manufacturer.Characteristics: high tear strength, picks up extremely fine details, low viscosity, good resistance to styrene attack, easy degassing..
Tensile Strength, Yield	2.70 MPa	391 psi	AVG Stress at Elongation M25; ASTM D412 Method A
Seals Eastern 5404 Nitrile Rubber General purpose NitrileInformation provided by Seals Eastern, Inc.