Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	600 MPa @Strain 0.200 %, Temperature -196 °C	87000 psi @Strain 0.200 %, Temperature -321 °F	EN min.; EN 10002-5
Outokumpu 4406 Cr-Ni-Mo Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar, and rod forms..
Tensile Strength, Yield	600 MPa @Strain 0.200 %, Temperature -196 °C	87000 psi @Strain 0.200 %, Temperature -321 °F	EN min.; EN 10002-5
Outokumpu 4429 Cr-Ni-Mo Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), cold rolled strip/sheet and rod forms.
Tensile Strength, Yield	600 MPa @Strain 0.200 %	87000 psi @Strain 0.200 %	as cast
Wieland Portadur P2 Casting Alloy Gold casting alloyApplications: inlays/onlays, crowns, short span bridges, long span bridges, telescopic and milling works, removable partials, acrylic veneeringDental
Tensile Strength, Yield	600 MPa @Strain 0.200 %	87000 psi @Strain 0.200 %	hardened
Wieland Portadur P2 Casting Alloy Gold casting alloyApplications: inlays/onlays, crowns, short span bridges, long span bridges, telescopic and milling works, removable partials, acrylic veneeringDental
Tensile Strength, Yield	600 MPa @Strain 0.200 %	87000 psi @Strain 0.200 %	hardened
Wieland Simidur S 1S PFM Alloy Palladium-base ceramic alloyApplications: crowns, short span bridges, long span bridges, telescopic and milling work, removable partials, ceramic veneering, acrylic veneeringDental
Tensile Strength, Yield	600 MPa @Strain 0.200 %	87000 psi @Strain 0.200 %	Q&T
Crucible Compaction Metals P/M 625 Corrosion Resistant Alloy P/M 625 (chemically, UNS N06625) is produced by the Crucible P/M process: inert gas atomization, coupled with consolidation by hot isostatic pressing (HIP) and/or extrusion. The Crucible powder con..