Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 586 MPa @Temperature 82.2 °C |
85000 psi @Temperature 180 °F |
0° Direction, Wet; Autoclave Cured; ASTM D3039-95 |
Park Electrochemical Nelcote® E-765 Epoxy Prepreg, T300 6K 5HS Reinforced Nelcote® E-765 is a tough 250°F cure prepreg system designed to replace 350°F cure systems in aircraft structural applications. FAA-approved Design Allowable Databases are available upon request... |
|||
Tensile Strength, Yield | >= 586 MPa @Strain 0.200 %, Thickness 25.4 - 38.1 mm |
>= 85000 psi @Strain 0.200 %, Thickness 1.00 - 1.50 in |
ASTM E-8 |
H.C. Starck 3403 Molybdenum Alloy APT-3 TZM, Arc-Cast Plate Arc-Cast Plate 3403Description of Product: This specification covers rolled plate of carbon-deoxidized TZM alloy (molybdenum + 0.5% titanium + 0.08% zirconium) produced from sheet bar consolidated .. |
|||
Tensile Strength, Yield | >= 586 MPa @Diameter 28.57 - 47.63 mm, Strain 0.200 % |
>= 85000 psi @Diameter 1.125 - 1.875 in, Strain 0.200 % |
ASTM E-8 |
H.C. Starck Molybdenum Alloy PBT, Bar Powder Metallurgy BarDescription of Product: This specification covers molybdenum alloy (Molybdenum + 0.5% titanium + 0.1% zirconium) wrought bar produced from pressed and sintered powder metallurg.. |
|||
Tensile Strength, Yield | >= 586 MPa @Diameter 28.57 - 47.63 mm, Strain 0.200 % |
>= 85000 psi @Diameter 1.125 - 1.875 in, Strain 0.200 % |
ASTM E-8 |
H.C. Starck Molybdenum Alloy TZM ABT, Arc-Cast Bar Description of Product: This specification covers carbon-deoxidized TZM alloy (molybdenum + 0.5% titanium + 0.08% zirconium) wrought bar produced from ingots consolidated by the H.C. Starck consuma.. |
|||
Tensile Strength, Yield | >= 586 MPa @Strain 0.200 %, Thickness 0.508 - 1.52 mm |
>= 85000 psi @Strain 0.200 %, Thickness 0.0200 - 0.0600 in |
ASTM E-8 |
H.C. Starck 3202 Pure Molybdenum ASL, Arc-Cast, Low Carbon Sheet Arc-Cast Sheet 3202 Low CarbonDescription of Product: This specification covers rolled sheet of carbon-deoxidized molybdenum produced from sheet bar consolidated by the H.C. Starck consumable elect.. |
|||
Tensile Strength, Yield | 586 MPa @Strain 0.200 %, Diameter 12.7 mm |
85000 psi @Strain 0.200 %, Diameter 0.500 in |
As Welded |
Haynes 282® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
Tensile Strength, Yield | 586 MPa @Temperature 249 °C |
85000 psi @Temperature 480 °F |
Cold Worked |
ATI Wah Chang TI-3Al-2.5V Ti-3Al-2.5V has proved to be a sufficiently malleable material for tube manufacture. It can be cold worked by standard tube making processes, is weldable and can be strength-ended by cold working an.. |