H.C. Starck Molybdenum Alloy TZM ABT, Arc-Cast Bar

Category Metal , Nonferrous Metal , Molybdenum Alloy , Refractory Metal
Manufacturer H.C. Starck
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF H.C. Starck Molybdenum Alloy TZM ABT, Arc-Cast Bar.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description of Product: This specification covers carbon-deoxidized TZM alloy (molybdenum + 0.5% titanium + 0.08% zirconium) wrought bar produced from ingots consolidated by the H.C. Starck consumable electrode vacuum-arc-casting process.Structure: Bar will be supplied in a stress-relieved condition, Material can also be supplied in the recrystallized condition.Information provided by H.C. Starck.
Mechanical Properties Metric English Comments
Hardness, Vickers <= 215

@Load 10.0 kg
 <= 215

@Load 22.0 lb
 mid-radius, recrystallized bar, all sizes; DPH (10 kg)
235 - 285

@Load 10.0 kg,
Diameter 73.03 - 88.9 mm
 235 - 285

@Load 22.0 lb,
Diameter 2.875 - 3.50 in
 mid-radius; DPH (10 kg)
240 - 290

@Load 10.0 kg,
Diameter 47.63 - 73.03 mm
 240 - 290

@Load 22.0 lb,
Diameter 1.875 - 2.875 in
 mid-radius; DPH (10 kg)
245 - 300

@Load 10.0 kg,
Diameter 28.57 - 47.63 mm
 245 - 300

@Load 22.0 lb,
Diameter 1.125 - 1.875 in
 mid-radius; DPH (10 kg)
250 - 310

@Load 10.0 kg,
Diameter 22.2 - 28.57 mm
 250 - 310

@Load 22.0 lb,
Diameter 0.875 - 1.125 in
 mid-radius; DPH (10 kg)
260 - 320

@Load 10.0 kg,
Diameter 3.17 - 22.2 mm
 260 - 320

@Load 22.0 lb,
Diameter 0.125 - 0.875 in
 mid-radius; DPH (10 kg)
Tensile Strength >= 586 MPa

@Diameter 73.03 - 88.9 mm
 >= 85000 psi

@Diameter 2.875 - 3.50 in
 ASTM E-8
>= 621 MPa

@Diameter 47.63 - 73.03 mm
 >= 90000 psi

@Diameter 1.875 - 2.875 in
 ASTM E-8
>= 689 MPa

@Diameter 28.57 - 47.63 mm
 >= 100000 psi

@Diameter 1.125 - 1.875 in
 ASTM E-8
>= 758 MPa

@Diameter 22.2 - 28.57 mm
 >= 110000 psi

@Diameter 0.875 - 1.125 in
 ASTM E-8
>= 793 MPa

@Diameter 3.17 - 22.2 mm
 >= 115000 psi

@Diameter 0.125 - 0.875 in
 ASTM E-8
Tensile Strength, Yield >= 517 MPa

@Diameter 73.03 - 88.9 mm,
Strain 0.200 %
 >= 75000 psi

@Diameter 2.875 - 3.50 in,
Strain 0.200 %
 ASTM E-8
>= 552 MPa

@Diameter 47.63 - 73.03 mm,
Strain 0.200 %
 >= 80000 psi

@Diameter 1.875 - 2.875 in,
Strain 0.200 %
 ASTM E-8
>= 586 MPa

@Diameter 28.57 - 47.63 mm,
Strain 0.200 %
 >= 85000 psi

@Diameter 1.125 - 1.875 in,
Strain 0.200 %
 ASTM E-8
>= 655 MPa

@Diameter 22.2 - 28.57 mm,
Strain 0.200 %
 >= 95000 psi

@Diameter 0.875 - 1.125 in,
Strain 0.200 %
 ASTM E-8
>= 689 MPa

@Diameter 3.17 - 22.2 mm,
Strain 0.200 %
 >= 100000 psi

@Diameter 0.125 - 0.875 in,
Strain 0.200 %
 ASTM E-8
Elongation at Break >= 5.0 %

@Diameter 73.03 - 88.9 mm
 >= 5.0 %

@Diameter 2.875 - 3.50 in
 ASTM E-8
>= 10 %

@Diameter 28.57 - 47.63 mm
 >= 10 %

@Diameter 1.125 - 1.875 in
 ASTM E-8
>= 10 %

@Diameter 47.63 - 73.03 mm
 >= 10 %

@Diameter 1.875 - 2.875 in
 ASTM E-8
>= 15 %

@Diameter 22.2 - 28.57 mm
 >= 15 %

@Diameter 0.875 - 1.125 in
 ASTM E-8
>= 18 %

@Diameter 3.17 - 22.2 mm
 >= 18 %

@Diameter 0.125 - 0.875 in
 ASTM E-8
Component Elements Properties Metric English Comments
Carbon, C 0.010 - 0.030 %
0.010 - 0.030 %
Iron, Fe <= 0.010 %
<= 0.010 %
Molybdenum, Mo >= 99.25 %
>= 99.25 %
by difference
Nickel, Ni <= 0.0020 %
<= 0.0020 %
Nitrogen, N <= 0.0020 %
<= 0.0020 %
Oxygen, O <= 0.0030 %
<= 0.0030 %
Silicon, Si <= 0.010 %
<= 0.010 %
Titanium, Ti 0.40 - 0.55 %
0.40 - 0.55 %
Zirconium, Zr 0.060 - 0.12 %
0.060 - 0.12 %