Polymer Property : Tensile Strength, Yield = 54000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	372 MPa @Temperature 23.9 °C	54000 psi @Temperature 75.0 °F	0° Direction, Dry; Oven Cure, 90min, 260°F; ASTM D638
Park Electrochemical Nelcote® F-529 Phenolic Prepreg, 7781 E-Glass Reinforced Nelcote® F-529 is a non-halogenated phenolic resin designed specifically for use in aircraft and mass-transit interior laminate and sandwich panels. F-529 was formulated for applications requiring ..
Tensile Strength, Yield	372 MPa @Strain 0.200 %, Thickness 12.7 mm	54000 psi @Strain 0.200 %, Thickness 0.500 in
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 760Â°C (1400Â°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Tensile Strength, Yield	372 MPa @Thickness 25.4 mm, Temperature 20.0 Â°C	54000 psi @Thickness 1.00 in, Temperature 68.0 Â°F	0.2% offset
Haynes HastelloyÂ® C-2000Â® alloy, flat products Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h..
Tensile Strength, Yield	372 MPa @Thickness 23.4 mm, Temperature 20.0 Â°C	54000 psi @Thickness 0.921 in, Temperature 68.0 Â°F	0.2% offset
Haynes HastelloyÂ® C-22Â® alloy, transverse, GMAW short arc weldment, plate HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..