Polymer Property : Tensile Strength, Yield = 42000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	290 MPa @Temperature 71.1 °C	42000 psi @Temperature 160 °F	0° Direction, Wet; ASTM D638
Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 120 E-Glass Reinforced Nelcote® E-761 is a versatile self-adhesive epoxy matrix for use in aerospace and commercial application where ease of processing and cost are key considerations.Key Features and Benefits:Controlle..
Tensile Strength, Yield	290 MPa @Temperature 71.1 °C	42000 psi @Temperature 160 °F	0° Direction, Dry; Autoclave, 50 psi, 90min; ASTM D638
Park Electrochemical Nelcote® F-529 Phenolic Prepreg, 7781 E-Glass Reinforced Nelcote® F-529 is a non-halogenated phenolic resin designed specifically for use in aircraft and mass-transit interior laminate and sandwich panels. F-529 was formulated for applications requiring ..
Tensile Strength, Yield	290 MPa @Thickness 3.17 mm	42000 psi @Thickness 0.125 in	LW
Industrial Laminates/Norplex NP841 Glass Fabric (discontinued **) Description: Woven glass fabric with phenolic resin. Contains Kocite® for controlled conductivity. Acts as static electricity drain to protect electrical and electronic equipment.Thickness Tested: ..
Tensile Strength, Yield	290 MPa @Thickness 1.57 mm	42000 psi @Thickness 0.0620 in	LW; ASTM D638
Industrial Laminates/Norplex NP504 Glass Fabric Description: Woven glass fabric with high temperature phenolic resin. Good flexural, compressive and impact strengths at elevated temperatures. Capable of continuous operation at 175Â° C, see note..
Tensile Strength, Yield	289.6 MPa @Thickness 2.00 mm, Temperature 204 Â°C	42000 psi @Thickness 0.0787 in, Temperature 399 Â°F	0.2% offset
Haynes HastelloyÂ® C-276 alloy, solution heat treated flat products HastelloyÂ® C-276 alloy is a nickel-molybdenum-chromium wrought alloy that is a versatile corrosion-resistant alloy. C-276 alloy is an improved wrought version of alloy C in that it usually doesn'..
Tensile Strength, Yield	289.6 MPa @Strain 0.200 %	42000 psi @Strain 0.200 %
ATI Allegheny Ludlum AL 468™ Dual Stabilized- Low Titanium Stainless Steel Characteristics:good corrosion resistance in a wide range of environments, can be used in annealed cold formed or as-welded conditions. Applications: used in place of Type 304 in an oxidizing when ..