Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 9.58 MPa | 1390 psi | ASTM D638 |
ExxonMobil Escorene® LD 722.MV Molding, extrusion and compounding resin
(discontinued **) Escorene Ultra LD 722.MV is a high vinyl acetate copolymer resin for specialty extrusion and compounding application. Articles made from LD 722.MV are soft and have excellent low temperature toughne.. |
|||
Tensile Strength at Break | 9.58 MPa | 1390 psi | ASTM D638 |
ExxonMobil Escorene® LD 767.MJ Molding, extrusion and compounding resin
(discontinued **) Escorene Ultra LD 767.MJ is a high viscosity, 29.5% vinyl acetate copolymer suitable for making very soft, blow molded or extruded articles with very good low temperature toughness. It can also be .. |
|||
Tensile Strength at Break | 9.58 MPa | 1390 psi | ASTM D412 |
Teknor Apex APEX® 1519-50 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMForms-PelletsFeatures- Good flexibility Information provided by Teknor Apex Company |
|||
Tensile Strength at Break | 9.58 MPa | 1390 psi | ASTM D412 |
Teknor Apex Telcar® OBC 4565A Thermoplastic Elastomer Uses: Flexible Grips; Overmolding Forms: Pellets Processing Method: Blow Molding; Profile Extrusion; Sheet Extrusion; Thermoforming; Wire and Cable Extrusion; Extrusion; Injection Molding Injection .. |
|||
Tensile Strength at Break | 9.58 MPa | 1390 psi | Across Flow; ASTM D412 |
ExxonMobil Santoprene® 121-80W175 Thermoplastic Elastomer A soft, black, UV resistant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance, and is designed for .. |