Polymer Property : Tensile Strength at Break = 40000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	241 - 276 MPa	35000 - 40000 psi	Nickel-Silver butt joint
Lucas-Milhaupt BRAZE 250 Silver Based Cadmium Free Filler Metal Characteristics:Braze 250 is an intermediate temperature silver brazing alloy with a long (325EF/180EC) melting range. It has a tendency to liquate (i.e. separate into low and high melting constitu..
Tensile Strength at Break	241 - 276 MPa	35000 - 40000 psi	Nickel-Silver butt joint
Lucas-Milhaupt BRAZE 300 Silver Based Cadmium Free Filler Metal Characteristics: Braze 300 is an intermediate temperature silver brazing alloy with a fairly long (160EF/70EC) melting range. This long melting range is helpful when wide gap joints are brazed and ..
Tensile Strength at Break	241 - 276 MPa	35000 - 40000 psi	Nickel-Silver butt joint
Lucas-Milhaupt BRAZE 541 Silver Based Cadmium Free Filler Metal Characteristics:Braze 541 is an intermediate temperature silver brazing alloy with a rather long, 235EF (130EC) melting range. It has a tendency to liquate (i.e. separate into low and high melting ..
Tensile Strength at Break	241 - 276 MPa	35000 - 40000 psi	Nickel-Silver butt joint
Lucas-Milhaupt BRAZE 716 (VTG) Grade 1 Silver Based Cadmium Free Filler Metal Characteristics: Braze 716 is a nickel modified silver copper eutectic filler metal. The addition of nickel renders this alloy somewhat more sluggish in flow characteristics than the eutectic comp..
Tensile Strength at Break	241 - 276 MPa	35000 - 40000 psi	Nickel-Silver butt joint
Lucas-Milhaupt BRAZE 716 (VTG) Grade 2 Silver Based Cadmium Free Filler Metal Characteristics: Braze 716 is a nickel modified silver copper eutectic filler metal. The addition of nickel renders this alloy somewhat more sluggish in flow characteristics than the eutectic comp..
Tensile Strength at Break	241 - 276 MPa	35000 - 40000 psi	Nickel-Silver butt joint
Lucas-Milhaupt BRAZE 720 Silver Based Cadmium Free Filler Metal Characteristics:Brazing 720 is the silver-copper eutectic composition and in melting it acts like a metallic element, i.e. it melts completely at a single temperature, thus it will quickly flow into..
Tensile Strength at Break	241 - 276 MPa	35000 - 40000 psi	Nickel-Silver butt joint
Lucas-Milhaupt BRAZE 721 (VTG) Grade 1 Silver Based Cadmium Free Filler Metal Applications: Braze 721, a VTG version of Braze 720, is designed for all types of moderate temperature vacuum systems and particularly where maximum precautions must be taken to insure the presenc..
Tensile Strength at Break	241 - 276 MPa	35000 - 40000 psi	Nickel-Silver butt joint
Lucas-Milhaupt BRAZE 721 (VTG) Grade 2 Silver Based Cadmium Free Filler Metal Applications: Braze 721, a VTG version of Braze 720, is designed for all types of moderate temperature vacuum systems and particularly where maximum precautions must be taken to insure the presenc..
Tensile Strength at Break	241 - 276 MPa	35000 - 40000 psi	Nickel-Silver butt joint
Lucas-Milhaupt SIL-FOS 5 Silver/ Copper/ Phosphorus Alloy Applications: Sil-Fos 5 was developed primarily for use on copper, but their use has extended to other nonferrous copper base alloys. It is used extensively on refrigeration units, air conditionin..
Tensile Strength at Break	207 - 276 MPa	30000 - 40000 psi	Brass butt joint
Lucas-Milhaupt BRAZE 560 Characteristics:Braze 560 is a low temperature, free-flowing brazing filler metal with a slight tendency to liquate (i.e. separate into low and high melting constituents) if heated slowly through it..