Polymer Property : Tensile Strength at Break = 37000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	255 MPa	37000 psi	Crosswise; ASTM D638
G-11 Fiberglass Epoxy Laminate Sheet This glass-epoxy laminate is specified for its extremely high strength and high dimensional stability over temperature. G-11 is used for terminal boards, high humidity applications, electrical and e..
Tensile Strength at Break	255 - 303 MPa	37000 - 44000 psi	Strip, Temper-Hard
Lucas-Milhaupt BRAZE 999 Commercial Grade Fine Silver Commercial grade fine silver (99.90% minimum silver) is widely used in numerous electrical, electronic, and industrial applications, such as contacts, fuse elements, lead wires, battery plated, and ..
Tensile Strength at Break	255 MPa	37000 psi	ISO 527 Type 1A
Solvay TECHNYLSTARâ„¢ AFX 218 V50 PA6, 50% glass filled, DRY Description TECHNYLSTARâ„¢ AFX 218 V50 is based on a patented high flow polyamide 66 resin (Technylstar), heat stabilized, reinforced with 50% of glass fiber, for injection molding. It is availab..
Tensile Strength at Break	255 MPa	37000 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON UEF26AS PPA (Europe-Africa-Middle East) LNP* Stat-kon* UEF26AS is a compound based on Polyphthalamide resin containing Glass Fiber, Carbon Fiber. Added features of this material include: Electrically Conductive.
Tensile Strength at Break	255 MPa	37000 psi	ISO 527-1/-2
DSM Stanyl® TW241F12 (DAM) Nylon 46 60% Glass Reinforced, Heat Stabilized, High Flow (North America) Information provided by DSM Engineering Plastics.
Tensile Strength at Break	255 MPa	37000 psi	ISO 527-1/-2
DSM Stanyl® TW241F12 Nylon 46-60% Glass Reinforced (European and Asian Grade) (Dry) Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temper..
Tensile Strength at Break	255 MPa	37000 psi	conditioned; ISO 527-1/-2
EMS-Grivory Grivory® GVL-6H nat PA*-GF60 Product description: Grivory GVL-6H natural is based on a combination of a heat stabilized semi-crystalline Polyamide with a partially aromatic Polyamide and 60% long glass fibers. Grivory GVL-6H na..
Tensile Strength at Break	255 MPa	37000 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® TSGL-50/4 black 9833 PA666-GF50 Product description: Grilon TSGL-50/4 black is based on a heat stabilized semicrystalline Polyamide PA66+PA6 and 50% long glass fibers. Grilon TSGL-50/4 black is characterized by the following key-p..
Tensile Strength at Break	255 MPa	37000 psi	5 [mm/min]; ISO 527-1/2
Akro-Plastic Akromid® T1 GF 50 (3101) PPA Conditioned, 50% Glass Filled The new AKROMID® T is characterized primarily by high heat resistance and the lowest moisture absorption of the three PA grades, making it particularly well-suited in the automotive sector for high..
Tensile Strength at Break	255 MPa @Temperature -40.0 °C	37000 psi @Temperature -40.0 °F	ASTM Test
BASF Ultramid® 8233G HS 33% Glass Filled PA6 (Conditioned) Ultramid 8233G HS is a heat stabilized, 33% glass fiber reinforced nylon 6 molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. It is also..
Tensile Strength at Break	255 MPa @Temperature -40.0 °C	37000 psi @Temperature -40.0 °F	ISO Data
BASF Ultramid® 8233G HS 33% Glass Filled PA6 (Conditioned) Ultramid 8233G HS is a heat stabilized, 33% glass fiber reinforced nylon 6 molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. It is also..
Tensile Strength at Break	255 MPa	37000 psi	ISO 527-1/-2
BASF Ultramid® A3W2G10 BK 20560 50% Glass Filled PA66 (Dry) Description: 50% glass fiber reinforced injection molding grade with optimized heat ageing performance for industrial articles having very high rigidity.Information provided by BASF