Polymer Property : Tensile Strength at Break = 3580 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	24.7 MPa	3580 psi	510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Flexible B7D01 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne
Tensile Strength at Break	24.7 MPa	3580 psi	ASTM D638
LyondellBasell PlexarÂ® PX2246 Extrudable Tie-Layer Resin - Anhydride Modified HDPE General DescriptionPlexarÂ® tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resin..
Tensile Strength at Break	24.7 MPa @Temperature 145 Â°C, Time 2100 sec	3580 psi @Temperature 293 Â°F, Time 0.583 hour	ASTM D412
LG Chemical SBR 1739 High Acrylonitrile Polymer Description: SBR 1739 is an oil extended cold polymerization SBR with 37.5 parts of Low PCA (PolyCyclic Aromatic) oil and styrene-butadiene copolymer of 40% bound styrene. Raw materials for this p..
Tensile Strength at Break	24.7 MPa @Temperature 145 Â°C, Time 2100 sec	3580 psi @Temperature 293 Â°F, Time 0.583 hour	ASTM D412
LG Chemical SBR 1789 High Acrylonitrile Polymer Description: SSBR 1789 is an oil extended cold polymerization SBR with 37.5 parts of Low PCA (RAE type) oil and styrene-butadiene copolymer of 40% bound styrene. Raw materials for this product are ..
Tensile Strength at Break	24.7 MPa	3580 psi	Transverse to Flow; ASTM D882
Diamond Polymers NPP10-0105 Vinyl Acetate Copolymer Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.