Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 238 MPa | 34500 psi | ASTM D638 |
Oxford Polymers PEEK-20CF-Black PEEK, 20% Carbon Fiber Reinforced Product Description: Carbon Fiber (20% Reinforced), PEEK, Polyetheretherketone, injection molding grade Processing and Delivery Form: Pellets and Injection MoldingAdditives: Carbon fiber Special Ch.. |
|||
Tensile Strength at Break | 238 MPa | 34500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON RE006 PA 66 LNP STAT-KON* RE006 is a compound based on Nylon 66 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength at Break | 238 MPa | 34500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP RC00A PA6.6 (Europe-Africa-Middle East) LNP* THERMOCOMP* RC00A is a compound based on PA6.6 resin containing Carbon Fiber. Added features include: Electrically Conductive |
|||
Tensile Strength at Break | 238 MPa | 34500 psi | ASTM D638 |
SABIC Innovative Plastics LNP VERTON UF-700-12 HS EXP PPA (Asia Pacific) LNP* Verton* UF-700-12 HS EXP is a compound based on Polyphthalamide resin containing Long Glass Fiber. Added features of this material include: Heat Stabilized. |