Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 15.0 MPa | 2180 psi | |
Plastcom SLOVALEN PQ 81 T 10 PP, 10% mineral filling FeaturesModified PP for injection moulding with the content of 10% mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased shrinkage. Gene.. |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | |
Plastcom SLOVALEN PQ 91T 5 PP, 5% mineral filling FeaturesModified PP for injection moulding with the content of 5 % mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased shrinkage. Gene.. |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM D412 |
Polimeri Europa Europrene® SOL T 177 Styrene - Butadiene Block Copolymer Europrene® SOL T 177 is a radial block copolymer obtained by anionic polymerization. The polymer is based on styrene and butadiene, where bound styrene is 50% weight. The polymer is extended with.. |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM D638 |
Braskem PB 525/64 LDPE Blown Film Extrusion Polyethylene
(discontinued **) 38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Automatic packaging of liquids products (FFS). Information provided by Braskem |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | |
LATI Latene® 11 MDT05-01 PP Homopolymer Polypropylene homopolymer (PPh) based compound. Magnetic detectable filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industr.. |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ISO 527-1, -2 |
LyondellBasell Hifaxâ„¢ ETA3081HS Thermoplastic Polyolefin Elastomer Description: Hifaxâ„¢ ETA3081HS medium melt flow, 800 MPa flexural modulus, paintable thermoplastic elastomeric olefin (TEO) resin has balanced physical properties, moldability and paintability. .. |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL WCP921 PPE-TPE (Europe-Africa-Middle East) Flexible Noryl* injection molding grade. Low specific gravity with good non-halogenated flame retardant performance. Developed for evaluation in overmolding applications such as plugs, strain relief.. |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | 50 mm/min, 1A; ISO 527 |
SABIC Innovative Plastics SABIC PPCOMPOUND 9712 PP SABIC® PPcompound 9712 is a mineral filled, impact modified polypropylene TPO. This material combines high impact resistance, scratch resistance, and heat stability with interior automotive UV st.. |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM D638 |
Teknor Apex APEX® 584 Polyvinyl Chloride, Flexible Notes: RoHS Compliant Features: General Purpose Uses: Tubing; Wire Jacketing Agency Ratings: UL 498; UL 62 Wire Types: SPT-1; SPT-2 Processing Method: Injection MoldingForms: PelletsInformation Prov.. |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp MB008S PP (Asia Pacific) LNP* Thermocomp* MB008S is a compound based on Polypropylene resin containing Glass Bead. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Asia Pa.. |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM D412 |
Sumitomo Chemical ESPOLEX® 901 Thermoplastic Elastomer ESPOLEX® TPE Series is a group of thermoplastic elastomers produced by Sumitomo Chemical Company. Among its material advantages, ESPOLEX® TPE Series is distinguished by offering many low-densi.. |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM D638 |
UBE F320 Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope.. |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | 500mm/min; ASTM D638 Type IV Specimen |
Westlake EMAC® SP2202 21.5% Ethylene-Methyl Acrylate Copolymer Westlake EMAC® SP2202 is a 21.5% EMA copolymer designed for blown film, tie-layers, and extrusions where flexibility, compatibility, or low heat seal temperatures are required. SP2202 provides exce.. |
|||
Tensile Strength at Break | >= 15.0 MPa | >= 2180 psi | 250mm/min; ISO 527 |
Borealis Visico™/Ambicat™ LE4427/LE4476 Polyethylene Compound, Crosslinkable Visico™ LE4427 / Ambicat™ LE4476 is a silane crosslinkable black compound designed for weather resistant covering/insulation of overhead and façade cables. The black base material Visico™ LE442.. |
|||
Tensile Strength at Break | >= 15.0 MPa | >= 2180 psi | ISO R 527 |
Fainplast Compounds FKA 89 Flexible PVC, Flame Retardant Insulation Lead Free Power cables |
|||
Tensile Strength at Break | >= 15.0 MPa | >= 2180 psi | ISO R 527 |
Fainplast Compounds GA 87/1 Flexible PVC, Flame Retardant Sheathing General purposes |
|||
Tensile Strength at Break | >= 15.0 MPa | >= 2180 psi | ISO R 527 |
Fainplast Compounds HGKA 83 Flexible PVC, Sheathing for High Temperatures Lead Free Operating temperature 90°C |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ISO R 527 |
Fainplast Compounds FAINGUM 6530 Flexible PVC, Injection Molding for Footwear Soles with rubber |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ISO R 527 |
Fainplast Compounds PH 75/UV Flexible PVC, Transparent Extrusion Transparent profiles UV resistant |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM D638 |
Aclo Accutech Polyethylene HD0234G20UVL High Density Glass Reinforced UV Stabilized |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM-D638 |
Braskem LD5000A LDPE Blow Molding Polyethylene LD5000A is a low-density polyethylene with good mechanical properties, good ESCR, and excellent sealing characteristics. It does not contain additives. It is used in general purpose blow molded arti.. |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ISO R 527 |
Addiplast Addilene J 380 Polypropylene Copolymer High impact strength, high elongation at breakInformation provided by Addiplast. |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM D257 |
3M BBI-A Shrinkable Tubing for Bus Bar 3M Heat Shrinkable Tubing for Bus Bar BBI-A Series is designed for insulating rectangular, square and round bus bar rated from 5 kV through 35 kV. It will also cover and insulate inline bolted conne.. |
|||
Tensile Strength at Break | 15.0 - 30.0 MPa | 2180 - 4350 psi | TM-019G |
AorTech Biomaterials Elast-Eon™ E5-325 Biomedical Polyurethane Pellets Elast-Eon™ 5-325 is a polyurethane with a 32.5% hard segment content and a mixed polyether/siloxane soft segment. It comes in pellet form. The pellets are colorless to yellowish and are soluble in .. |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM D638 |
Arkema Group LOTRYL® 14 MGC 02 Copolymer Ethylene - Methyl Acrylate LOTRYL® 14 MGC 02 is a random copolymer of ethylene and methyl acrylate made by high-pressure radicalar polymerisation process. Due to the Methyl Acrylate content, LOTRYL® 14 MGC 02 is a polymer o.. |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ISO R 527 |
Addiplast Addilene PMD 50284 Polypropylene Copolymer Mineral reinforced, improved rigidityInformation provided by Addiplast. |
|||
Tensile Strength at Break | >= 15.0 MPa | >= 2180 psi | ISO R 527 |
Fainplast Compounds AP 90/2 Flexible PVC, Flame Retardant Insulation General purposes |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON MS000IL PP LNP* STAT-KON* MS000IL is a compound based on Polypropylene resin containing Stainless Steel. Added features of this material include: High Impact, Low Extractible, Electrically Conductive, food c.. |