- HOME
- POLYMER SEARCH
- Polymer Property : Tensile Strength at Break = 12.0 MPa
Polymer Property : Tensile Strength at Break = 12.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D412 |
| Polimeri Europa Europrene® SOL T 190 Styrene - Isoprene Block Copolymer Europrene® SOL T 190 is a linear block copolymer obtained by anionic polymerization. The polymer is based on styrene and isoprene, where bound styrene content is 16% weight and diblock content is .. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 |
| SABIC MG200024 Linear Low Density Polyethylene for Compounding Product Description: MG200024 is a Linear Low Density Polyethylene grade with a narrow molecular weight distribution primarily suitable for compounding. It is in the powder form designed to give g.. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ISO 527 |
| Polimeri Europa Riblene® GM 20 Low Density Polyethylene - Coating Grade Riblene GM 20 is a medium fluidity low density polyethylene resin (LDPE).Main Applications: Riblene GM 20 is suitable for coating applications where a low neck-in is required. Moreover, for its rh.. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ISO 527 |
| Polimeri Europa Riblene® GM 20 R Low Density Polyethylene - Coating Grade Riblene GM 20 R is a medium fluidity low density polyethylene resin (LDPE).Main Applications: Riblene GM 20 R is suitable for coating applications where a low neck-in is required. Moreover, for it.. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | 500mm/min; ASTM D638 Type IV Specimen |
| Westlake EMAC® SP2405 20% Ethylene-Methyl Acrylate Copolymer
(discontinued **) Westlake EMAC® SP2405 is a 20% EMA copolymer designed for blown or cast film, tie-layers, and extrusions where flexibility, compatibility, or low heat seal temperature are required. SP2405 provides.. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | 500 mm/min; ASTM D638 |
| Eastman D4027-P Voridian Polyethylene
(discontinued **) VORIDIAN low density polyethylene D4027-P is a formulation suggested for extrusion coating applications that require clarity, high gloss and superior hot tack properties. Applications/UsesFood Packa.. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | Extruded wire; ASTM D412 |
| DuPont Elvax® 40L-03 Low Smoke Non-halogen Jacket Formulation
(discontinued **) Elvax® 40L-03 low smoke non-halogen jackets.Information provided by DuPont. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | Extruded wire; ASTM D412 |
| DuPont Elvax® 40L-08 Low Smoke Non-Halogen Jacket Formulation
(discontinued **) Elvax® 40L-08 low smoke non-halogen jackets.Information provided by DuPont. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | 200mm/min; ASTM D638 |
| LG Chemical LUTENE LB5000 LDPE Extrusion Coating Description: LUTENE LB5000 is mainly intended for extrusion coating and can be processed at high speed uniform thickness and width. LUTENE LB5000 is also noted for the excellent adhesion to porous a.. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP FL003 PE LNP* LUBRICOMP* FL003 is a compound based on Polyethylene resin containing 15% PTFE. Added features include: Internally Lubricated. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 |
| Solvay Specialty Polymers Cogegum® GFR/340-HP Polyolefin Cogegum® XLPO-HFFR - Crosslinkable Halogen Free Fire Retardant compound. Silane grafted compound moisture curable by addition of a catalyst masterbatch (Sioplas® method). It consists of a poly.. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D412 |
| Sumitomo Chemical ESPOLEX® WT318 Thermoplastic Elastomer ESPOLEX® TPE Series is a group of thermoplastic elastomers produced by Sumitomo Chemical Company. Among its material advantages, ESPOLEX® TPE Series is distinguished by offering many low-densi.. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | 500 mm/min; ASTM D638 Type IV Specimen |
| Westlake EMAC® SP2258 17% Ethylene-Methyl Acrylate Copolymer Westlake EMAC® SP2258 is a 17% EMA copolymer containing slip and antiblock. This resin is designed for blown or cast film, tie-layers, and extrusions where flexibility, compatibility, or low heat s.. |
|||
| Tensile Strength at Break | >= 12.0 MPa | >= 1740 psi | 50 mm/min; ISO 527 |
| Fainplast Compounds Ethylplus 600 Polyethylene Cable Compound Polyethelene, halogen-free cable compound with superior thermo-mechanical properties, outstanding heat resistance, and high electrical propertiesSolid LDPEInformation provided by Fainplast Compounds.. |
|||
| Tensile Strength at Break | >= 12.0 MPa | >= 1740 psi | ISO R 527 |
| Fainplast Compounds FR 70 Flexible PVC, Insulation Good flexibility cables |
|||
| Tensile Strength at Break | >= 12.0 MPa | >= 1740 psi | ISO R 527 |
| Fainplast Compounds FR 75 Flexible PVC, Insulation General purposes |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ISO R 527 |
| Fainplast Compounds GS 70 Flexible PVC, Injection Molding for Footwear Soles and heels |
|||
| Tensile Strength at Break | >= 12.0 MPa | >= 1740 psi | ISO R 527 |
| Fainplast Compounds GS 77 Flexible PVC, Electrical Plugs Plugs |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | IEC 60811 |
| Fainplast Compounds HAX HF 36/O Halogen Free PVC General purpose |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | IEC 60811 |
| Fainplast Compounds HAX HF 4021/TC Halogen Free PVC Improved flame retardancy |
|||
| Tensile Strength at Break | >= 12.0 MPa | >= 1740 psi | ISO R 527 |
| Fainplast Compounds CKL 86 Flexible PVC, Sheathing Lead Free General purposes |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ISO R 527 |
| Fainplast Compounds MPH 62 Medical Flexible PVC, Extrusion Tubolar apparatus and peristaltic pump segments |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ISO R 527 |
| Fainplast Compounds PM 7010 Flexible PVC, Extrusion Pipes and profiles |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 |
| Braskem BF 2021 LDPE Cast Film Extrusion Polyethylene 38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Films for absorbents and diapers (with HDPE and LLDPE); general purpose. Information provi.. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 |
| Aclo Accutech Polypropylene Copolymer CP0437C10L Calcium Reinforced |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 |
| Azdel SuperLite® SL551000-100 PP Resin Matrix / 55% Glass Fiber (4.5 mm Molded Thickness) AZDEL SuperLite® SL551000-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | |
| AorTech Biomaterials Elast-Eon™ E5-130 Biomedical Polyurethane Pellets Elast-Eon™ polymers are used in biomedical applications. They have high biostability so they can be used for long term implantation. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ISO R 527 |
| Fainplast Compounds PM 60/K Flexible PVC, Extrusion Profiles low migration |
|||