Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 700 MPa @Temperature 650 °C |
102000 psi @Temperature 1200 °F |
|
Special Metals UDIMET® alloy 188 Cobalt-base Alloy UDIMET® alloy 188 (UNS R30188) is a cobalt-base alloy with excellent high-temperature strength and good oxidation resistance to 2000°F (1093°C). The high chromium level coupled with small .. |
|||
Tensile Strength at Break | >= 700 MPa | >= 102000 psi | |
Goodfellow Cobalt/Boron/Silicon/Iron/Molybdenum/Nickel Alloy Information provided by Goodfellow. |
|||
Tensile Strength at Break | >= 700 MPa | >= 102000 psi | |
Goodfellow Cobalt/Silicon/Boron/Iron/Nickel Alloy Metallic glasses (glassy alloys) or amorphous metals. Uses include soft magnetic applications, brazing, coating and as reinforcing fibers.Information provided by Goodfellow. |
|||
Tensile Strength at Break | >= 700 MPa | >= 102000 psi | |
Goodfellow Iron 40/Nickel 38/Boron 18 Alloy Metallic glass (glassy alloy) or amorphous metal. Uses include soft magnetic applications, brazing, coating and as reinforcing fibers.Information provided by Goodfellow. |
|||
Tensile Strength at Break | >= 700 MPa | >= 102000 psi | |
Goodfellow Iron 78/Boron 13/Silicon 9 Alloy Information provided by Goodfellow. |
|||
Tensile Strength at Break | >= 700 MPa | >= 102000 psi | |
Goodfellow Iron 81/Boron 13.5/Silicon 3.5 Alloy Information provided by Goodfellow. |
|||
Tensile Strength at Break | 700 - 880 MPa | 102000 - 128000 psi | |
ThyssenKrupp PAS 650 Structural Steel for Cold Forming This Material Specification applies to plates made of low carbon high strength steels with minimum yield strength values between 315 and 700 MPa1) in the thermo mechanically rolled delivery conditio.. |
|||
Tensile Strength at Break | 703 MPa @Temperature 760 °C, Time 7.20e+6 sec |
102000 psi @Temperature 1400 °F, Time 2000 hour |
Room Temperature properties after Isothermal Exposure |
Special Metals INCOLOY® alloy 803 Fe-Ni-Cr Alloy INCOLOY® alloy 803 (UNS S35045), an iron-nickel-chromium alloy, is designed for use in petrochemical, chemical and thermal processing applications. The nickel and chromium contents of alloy 803 ar.. |
|||
Tensile Strength at Break | 700 MPa @Temperature 650 °C |
102000 psi @Temperature 1200 °F |
|
Special Metals UDIMET® alloy L-605 Co-Cr-W-Ni Alloy UDIMET® alloy L-605 (UNS R30605) is a solid solution strengthened cobalt-chromium-tungsten-nickel alloy with excellent high-temperature strength and excellent oxidation resistance to 2000°F (1093°.. |