Polymer Property : Ball Indentation Hardness = 330 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	330 MPa	47900 psi	ISO 2039-1
Nilit FRIANYL A63 CV30 Nylon 6.6 for injection molding, 30% carbon fiber reinforced Nylon 6.6 for injection molding (good conductive and electrostatic properties).Information provided by Frisetta Polymer, which merged into Nilit Plastics
Ball Indentation Hardness	330 - 420 MPa	47900 - 60900 psi	Average value: 358 MPa Grade Count:9
Overview of materials for Nylon 66, 60% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 60% Glass Fiber Filled". Specific grades with glass content between 55% and 64% are included. ..
Ball Indentation Hardness	330 MPa	47900 psi	conditioned; ISO 2039-1
EMS-Grivory Grivory® GVX-65 H black 9915 PA*-GF65 Product description: Grivory GVX-65H black 9915 is a 65% glass fiber reinforced engineering thermoplastic material based on a combination of semicrystalline polyamide with partially aromatic copolya..
Ball Indentation Hardness	330 MPa	47900 psi	conditioned; ISO 2039-1
EMS-Grivory Grivory® GVX-65 H nat PA*-GF65 Product description: Grivory GVX-65H natural is a 65% glass-fiber reinforced engineering thermoplastic material based on a combination of semi-crystalline polyamide with partially aromatic copolyami..
Ball Indentation Hardness	330 - 350 MPa	47900 - 50800 psi	ISO 2032-N961
Adamas Rixon 130 PEEK, 30% Carbon Filled Information provided by Adamas, HPM
Ball Indentation Hardness	330 MPa	47900 psi	H 961/30; ISO 2039-1
Akro-Plastic Akroloy® PA GF 60 (2844) PA 6.6 & PA6I/6T Dry, 60% Glass Filled One of the most characteristic properties of polyamide (PA 6.6) is the absorption of moisture. This essentially leads to increased toughness and elongation at break, to name the most important param..
Ball Indentation Hardness	330 MPa	47900 psi	H 961/30; ISO 2039-1
Akro-Plastic Akromid® A3 GF 60 (2424) PA 6.6 Dry, 60% Glass Filled AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperat..
Ball Indentation Hardness	330 MPa	47900 psi	H 961/30; ISO 2039-1
Akro-Plastic Akromid® T1 GF 40 (3464) PPA Dry, 40% Glass Filled The new AKROMID® T is characterized primarily by high heat resistance and the lowest moisture absorption of the three PA grades, making it particularly well-suited in the automotive sector for high..