Polymer Property : Film Tensile Strength at Yield, MD = 20.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	20.0 MPa @Thickness 0.430 mm, Temperature 23.0 Â°C	2900 psi @Thickness 0.0169 in, Temperature 73.4 Â°F	ASTM D638
Mapal Plastics Maplon CFA-HK Polypropylene Sheet Applications: For use with electrical insulation products. For use when flame retardant and static dissipative properties are required.
Film Tensile Strength at Yield, MD	20.0 MPa @Thickness 0.250 mm, Temperature 23.0 Â°C	2900 psi @Thickness 0.00984 in, Temperature 73.4 Â°F	ASTM D638
Mapal Plastics Maplon CFA-HK Polypropylene Sheet Applications: For use with electrical insulation products. For use when flame retardant and static dissipative properties are required.
Film Tensile Strength at Yield, MD	20.0 MPa @Thickness 0.0200 mm	2900 psi @Thickness 0.000787 in	ISO 527-3
Total MDPE HF 513 Medium Density Polyethylene, Blown Film MDPE HF 513 is a medium density polyethylene produced by slurry loop low pressure process with hexene as co-monomer.MDPE HF 513 is a semi-high molecular weight polyethylene giving excellent mechanic..
Film Tensile Strength at Yield, MD	20.0 MPa @Thickness 0.0400 mm	2900 psi @Thickness 0.00157 in	ISO 527-3
Total MDPE HT 514 Medium Density Polyethylene, Blown Film MDPE HT 514 is a medium density polyethylene produced by slurry loop low pressure process with hexene as co-monomer.MDPE HT 514 is a semi-high molecular weight polyethylene giving excellent mechanic..