Mapal Plastics Maplon CFA-HK Polypropylene Sheet

Category Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Sheet/Thermoforming Grade
Manufacturer Mapal Plastics
Trade Name Maplon
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Mapal Plastics Maplon CFA-HK Polypropylene Sheet.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Applications: For use with electrical insulation products. For use when flame retardant and static dissipative properties are required.
Physical Properties Metric English Comments
Specific Gravity 1.03 g/cc

@Thickness 0.430 mm
 1.03 g/cc

@Thickness 0.0169 in
1.03 g/cc

@Thickness 0.250 mm
 1.03 g/cc

@Thickness 0.00984 in
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 20.0 MPa

@Thickness 0.430 mm,
Temperature 23.0 °C
 2900 psi

@Thickness 0.0169 in,
Temperature 73.4 °F
 ASTM D638
20.0 MPa

@Thickness 0.250 mm,
Temperature 23.0 °C
 2900 psi

@Thickness 0.00984 in,
Temperature 73.4 °F
 ASTM D638
Film Tensile Strength at Yield, TD 16.0 MPa

@Thickness 0.430 mm,
Temperature 23.0 °C
 2320 psi

@Thickness 0.0169 in,
Temperature 73.4 °F
 ASTM D638
16.0 MPa

@Thickness 0.250 mm,
Temperature 23.0 °C
 2320 psi

@Thickness 0.00984 in,
Temperature 73.4 °F
 ASTM D638
Film Elongation at Yield, MD 16 %

@Thickness 0.250 mm,
Temperature 23.0 °C
 16 %

@Thickness 0.00984 in,
Temperature 73.4 °F
 ASTM D638
18 %

@Thickness 0.430 mm,
Temperature 23.0 °C
 18 %

@Thickness 0.0169 in,
Temperature 73.4 °F
 ASTM D638
Film Elongation at Yield, TD 9.0 %

@Thickness 0.250 mm,
Temperature 23.0 °C
 9.0 %

@Thickness 0.00984 in,
Temperature 73.4 °F
 ASTM D638
14 %

@Thickness 0.430 mm,
Temperature 23.0 °C
 14 %

@Thickness 0.0169 in,
Temperature 73.4 °F
 ASTM D638
Modulus of Elasticity 0.300 GPa

@Thickness 0.430 mm,
Temperature 23.0 °C
 43.5 ksi

@Thickness 0.0169 in,
Temperature 73.4 °F
 TD; ASTM D638
0.350 GPa

@Thickness 0.250 mm,
Temperature 23.0 °C
 50.8 ksi

@Thickness 0.00984 in,
Temperature 73.4 °F
 TD; ASTM D638
0.350 GPa

@Thickness 0.430 mm,
Temperature 23.0 °C
 50.8 ksi

@Thickness 0.0169 in,
Temperature 73.4 °F
 ASTM D638
0.400 GPa

@Thickness 0.250 mm,
Temperature 23.0 °C
 58.0 ksi

@Thickness 0.00984 in,
Temperature 73.4 °F
 ASTM D638
Flexural Modulus 1.278 GPa

@Thickness 3.20 mm,
Temperature 23.0 °C
 185.4 ksi

@Thickness 0.126 in,
Temperature 73.4 °F
Izod Impact, Notched 0.500 J/cm

@Thickness 3.20 mm,
Temperature -20.0 °C
 0.937 ft-lb/in

@Thickness 0.126 in,
Temperature -4.00 °F
 ASTM D256
2.50 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 4.68 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Vicat Softening Point 150 °C

@Thickness 0.430 mm
 302 °F

@Thickness 0.0169 in
 ASTM D1525
150 °C

@Thickness 0.250 mm
 302 °F

@Thickness 0.00984 in
 ASTM D1525
Heat Distortion Temperature 85.0 °C

@Thickness 0.430 mm
 185 °F

@Thickness 0.0169 in
 ASTM 648
85.0 °C

@Thickness 0.250 mm
 185 °F

@Thickness 0.00984 in
 ASTM 648
Flammability, UL94 V-0

@Thickness 0.430 mm
 V-0

@Thickness 0.0169 in
Electrical Properties Metric English Comments
Surface Resistance 1.00e+9 ohm

@Thickness 0.430 mm
 1.00e+9 ohm

@Thickness 0.0169 in
 ASTM D257
1.00e+9 ohm

@Thickness 0.250 mm
 1.00e+9 ohm

@Thickness 0.00984 in
 ASTM D257
Dielectric Breakdown 15000 V

@Thickness 0.250 mm
 15000 V

@Thickness 0.00984 in
 ASTM D149
20000 V

@Thickness 0.430 mm
 20000 V

@Thickness 0.0169 in
 ASTM D149
Descriptive Properties Value Comments
Color Black