Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, MD | 55.0 MPa @Thickness 0.0400 mm |
7980 psi @Thickness 0.00157 in |
ISO 527-3 |
Total MDPE HF 513 Medium Density Polyethylene, Blown Film MDPE HF 513 is a medium density polyethylene produced by slurry loop low pressure process with hexene as co-monomer.MDPE HF 513 is a semi-high molecular weight polyethylene giving excellent mechanic.. |
|||
Film Tensile Strength at Break, MD | 55.0 MPa @Thickness 0.0400 mm |
7980 psi @Thickness 0.00157 in |
ISO 527-3 |
Total MDPE HR 515 Medium Density Polyethylene, Blown Film MDPE HR 515 is a medium density polyethylene produced with hexene as a co-monomer. It shows a broad molecular weight distribution ensuring outstanding processability.MDPE HR 515 is especially dedic.. |