Total MDPE HR 515 Medium Density Polyethylene, Blown Film

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , MDPE , Medium Density Polyethylene (MDPE), Film Grade
Manufacturer	Total Atofina
Trade Name	MDPE
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total MDPE HR 515 Medium Density Polyethylene, Blown Film.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

MDPE HR 515 is a medium density polyethylene produced with hexene as a co-monomer. It shows a broad molecular weight distribution ensuring outstanding processability.MDPE HR 515 is especially dedicated to high rigidity film applications, particularly in blend and/or coextrusion with LDPE and/or LLDPE.MDPE HR 515 is suited for many applications, in the field of consumer, food or hygiene packaging.Information provided by Total Petrochemicals.

Physical Properties	Metric	English	Comments
Specific Gravity	0.942 g/cc	0.942 g/cc	ISO 1183
Melt Flow	0.22 g/10 min @Load 2.16 kg, Temperature 190 °C	0.22 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
	17.5 g/10 min @Load 21.6 kg, Temperature 190 °C	17.5 g/10 min @Load 47.6 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	22.0 MPa @Thickness 0.0400 mm	3190 psi @Thickness 0.00157 in	ISO 527-3
	23.0 MPa @Thickness 0.0200 mm	3340 psi @Thickness 0.000787 in	ISO 527-3
Film Tensile Strength at Yield, TD	22.0 MPa @Thickness 0.0400 mm	3190 psi @Thickness 0.00157 in	ISO 527-3
	24.0 MPa @Thickness 0.0200 mm	3480 psi @Thickness 0.000787 in	ISO 527-3
Film Elongation at Break, MD	450 % @Thickness 0.0200 mm	450 % @Thickness 0.000787 in	ISO 527-3
	580 % @Thickness 0.0400 mm	580 % @Thickness 0.00157 in	ISO 527-3
Film Elongation at Break, TD	540 % @Thickness 0.0200 mm	540 % @Thickness 0.000787 in	ISO 527-3
	660 % @Thickness 0.0400 mm	660 % @Thickness 0.00157 in	ISO 527-3
Flexural Modulus	0.810 GPa @Strain <=0.250 %	117 ksi @Strain <=0.250 %	ISO 178
Elmendorf Tear Strength, MD	0.800 g/micron @Thickness 0.0200 mm	20.3 g/mil @Thickness 0.000787 in	ISO 6383-2
	1.20 g/micron @Thickness 0.0400 mm	30.5 g/mil @Thickness 0.00157 in	ISO 6383-2
Elmendorf Tear Strength, TD	13.3 g/micron @Thickness 0.0200 mm	338 g/mil @Thickness 0.000787 in	ISO 6383-2
	15.3 g/micron @Thickness 0.0400 mm	389 g/mil @Thickness 0.00157 in	ISO 6383-2
Dart Drop Test	145 g @Thickness 0.0200 mm	0.320 lb @Thickness 0.000787 in	ISO 7765-1
	190 g @Thickness 0.0400 mm	0.419 lb @Thickness 0.00157 in	ISO 7765-1
Film Tensile Strength at Break, MD	55.0 MPa @Thickness 0.0400 mm	7980 psi @Thickness 0.00157 in	ISO 527-3
	65.0 MPa @Thickness 0.0200 mm	9430 psi @Thickness 0.000787 in	ISO 527-3
Film Tensile Strength at Break, TD	51.0 MPa @Thickness 0.0400 mm	7400 psi @Thickness 0.00157 in	ISO 527-3
	53.0 MPa @Thickness 0.0200 mm	7690 psi @Thickness 0.000787 in	ISO 527-3

Thermal Properties	Metric	English	Comments
Melting Point	127 °C	261 °F	ISO 11357
Vicat Softening Point	124 °C	255 °F	ISO 306

Processing Properties	Metric	English	Comments
Processing Temperature	190 - 220 °C	374 - 428 °F	Extrusion