Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 89.2 MPa | 12900 psi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® UF-1013 PC, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 89.2 MPa | 12900 psi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® UF-1017 PC, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 89.2 MPa | 12900 psi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® UF-1017B PC, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 89.2 MPa | 12900 psi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® UF-1017S PC, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 89.2 MPa | 12900 psi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® UF-1017 PC, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 89.2 MPa | 12900 psi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® UF-1017B PC, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 89.2 MPa | 12900 psi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® UF-1013 PC, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 89.2 MPa | 12900 psi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® UF-1017S PC, Unreinforced FR Information provided by Samsung Cheil Industries. |