Polymer Property : Flexural Strength = 420 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	420 MPa	60900 psi
Plastcom SLOVAMID 6 GF 65/1M PA6 reinforced with 65% glass fibre Features: PA 6 for injection moulding, chemically strengthened with 65% of glass fibre, for mouldings with high strength and toughness used in the automotive, electrical, engineering and consumer-go..
Flexural Strength	420 MPa	60900 psi	ISO 178
PolyOne OnForce™ LFT AM-60LGF/001 Natural Polyphthalamide (PPA) PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. ..
Flexural Strength	420 MPa	60900 psi	ISO 178
PolyOne OnForce™ LFT NN-40LCF/001 Grey Polyamide 66 (Nylon 66) PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. ..
Flexural Strength	420 MPa	60900 psi	STN EN ISO 178
Plastcom SLOVAMID® 6 GF 65/2M PA6 reinforced with glass fiber PA 6 for injection molding, reinforced with 65% of glass fiber, for moldings used in the automotive, electrical, engineering and consumer-goods industry. Application: grips of electrotools, hobby to..
Flexural Strength	420 MPa	60900 psi	0°; measured on 0.1" panel molded from tape; ASTM D790
Polystrand ThermoPro™ IE6010 Unitape Unidirectional Polypropylene-Glass Composite Fiber Orientation is 0°.Polystrand ThermoPro™ combines continuous E-Glass (ThermoPro-E™) structural reinforcing fibers in either a polyethylene or polypropylene proprietary thermoplastic polymer ..
Flexural Strength	420 MPa	60900 psi
Lehmann & Voss LUVOCOMÂ® 20-8171 Polyphthalamide, with carbon fiber and glass fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Electrically conductive, suita..
Flexural Strength	420 MPa	60900 psi
Lehmann & Voss LUVOCOMÂ® 1/XCF/25 Polyamide 66, with carbon fiber, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Reduced moment of inertia comp..
Flexural Strength	420 MPa	60900 psi	Bending Strength; 4-Point Method (40x4x3 mm³); ASTM-F417
CeramTec Alunit® HS Aluminum Nitride Alunit® HS offers an extremely high thermal conductivity of 170 W/mK and outstanding electrical insulation properties. The thermal expansion coefficient of this material is comparable to silicon. I..
Flexural Strength	420 MPa	60900 psi	Bending Strength; ASTM-F417
CeramTec Rubalit® 708 Alumina, 96% Based on 96% aluminum oxide, Rubalit® 708 was developed specifically for making heavy-duty resistors and miniature metal layer resistors. Because of its outstanding strength, this same material is ..
Flexural Strength	420 MPa	60900 psi	ASTM-D790
Polyram Polytron A50B02 Nylon 66, Chemically Coupled 50% Long Fiber A CHEMICALLY COUPLED 50% LONG FIBER GLASS REINFORCED BLACK NYLON 6.6 HEAT STABILIZED, UV STABILIZED FOR INJECTIONInformation provided by Polyram Ram On Ind.
Flexural Strength	420 MPa	60900 psi	DAM; ISO 178
DuPont Performance Polymers Zytel® HTN 55G55LWSF BK752A Polyphthalamide (PPA) 55% Glass Reinforced PPA High Performance Polyamide with Low Warpage and High Stiffness Information provided by DuPont Performance Polymers
Flexural Strength	420 MPa	60900 psi	ASTM-D790
Polyram Polytron A50N02 Nylon 66, Chemically Coupled 50% Long Fiber A CHEMICALLY COUPLED 50% LONG FIBER GLASS REINFORCED NATURAL NYLON 6.6 HEAT STABILIZED, UV STABILIZED FOR INJECTIONInformation provided by Polyram Ram On Ind.