Polymer Property : Flexural Strength = 405 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	405 MPa	58700 psi	ASTM D-790
PlastiComp Complet® LCF20/LGF20 – PA66 BLK Polyamide 66, 40% Long Carbon/Glass Fiber Composite PelletsInformation provided by PlastiComp, Inc.
Flexural Strength	405 MPa	58700 psi
Lehmann & Voss LUVOCOMÂ® 1105-8179 PEEK, with carbon fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High-strength and high-stiff parts; low coefficient of expansion.Dynamic stressed parts at..
Flexural Strength	405 MPa	58700 psi
Lehmann & Voss LUVOCOMÂ® 20-7638 Polyphthalamide, with carbon fiber and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Low influence from moisture an..
Flexural Strength	405 MPa	58700 psi
Lehmann & Voss LUVOCOMÂ® 1105/XCF/25 PEEK, with carbon fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High-strength and high-stiff parts; low coefficient of expansion.Dynamic stressed parts at..
Flexural Strength	405 MPa	58700 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP VERTON RV00AEXP PA 66 (Europe-Africa-Middle East) LNP* VERTON* RV00AEXP is a compound based on PA 66 resin containing Long Glass Fiber.
Flexural Strength	405 MPa	58700 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP VERTON RV00ASXP PA 66 (Europe-Africa-Middle East) LNP* VERTON* RV00ASXP is a compound based on PA 66 resin containing Long Glass Fiber. Added features include; Heat Stabilized.
Flexural Strength	405 MPa	58700 psi	2 [mm/min]; ISO 178
Akro-Plastic Akroloy® PA GF 60 (2844) PA 6.6 & PA6I/6T Dry, 60% Glass Filled One of the most characteristic properties of polyamide (PA 6.6) is the absorption of moisture. This essentially leads to increased toughness and elongation at break, to name the most important param..
Flexural Strength	405 MPa	58700 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP VERTON RV00ASXS PA 66 (Europe-Africa-Middle East) LNP* VERTON* RV00ASXS is a compound based on PA 66 resin containing Long Glass Fiber. Added features include; Heat Stabilized
Flexural Strength	405 MPa	58700 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP VERTON RV00AXX9 PA 66 (Europe-Africa-Middle East) LNP* VERTON* RV00AXX9 is a compound based on PA 66 resin containing Long Glass Fiber.