SABIC Innovative Plastics LNP VERTON RV00AEXP PA 66 (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP VERTON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP VERTON RV00AEXP PA 66 (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* VERTON* RV00AEXP is a compound based on PA 66 resin containing Long Glass Fiber.
Physical Properties Metric English Comments
Density 1.57 g/cc
0.0567 lb/in³
ISO 1183
Water Absorption 0.80 %

@Time 86400 sec
0.80 %

@Time 24.0 hour
ISO 62-1
Linear Mold Shrinkage, Flow 0.0024 cm/cm

@Time 86400 sec
0.0024 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0079 cm/cm

@Time 86400 sec
0.0079 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 268 MPa
38900 psi
5 mm/min; ISO 527
Elongation at Break 2.0 %
2.0 %
5 mm/min; ISO 527
Tensile Modulus 17.6 GPa
2550 ksi
1 mm/min; ISO 527
Flexural Strength 405 MPa
58700 psi
2 mm/min; ISO 178
Flexural Modulus 15.5 GPa
2250 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 35.0 kJ/m²
16.7 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 100 kJ/m²
47.6 ft-lb/in²
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 24.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
13.3 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
CTE, linear, Transverse to Flow 54.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
30.0 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 265 °C
509 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 262 °C
504 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
UL RTI, Electrical 105 °C
221 °F
UL 746B
UL RTI, Mechanical with Impact 110 °C
230 °F
UL 746B
UL RTI, Mechanical without Impact 110 °C
230 °F
UL 746B
Flammability, UL94 HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
UL 94
Electrical Properties Metric English Comments
Comparative Tracking Index >= 600 V
>= 600 V
IEC 60112
Hot Wire Ignition, HWI >= 120 sec
>= 120 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A