Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 238 MPa | 34500 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP RFL36SXC PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RFL36SXC is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Heat Stabilized. |
|||
Flexural Strength | 238 MPa | 34500 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP RFL36SXD PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RFL36SXD is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Heat Stabilized. |
|||
Flexural Strength | 238 MPa | 34500 psi | ISO 178 |
Solvay Specialty Polymers KetaSpire® KT-880 GF20 Polyetheretherketone (PEEK), 20% Glass Fiber KetaSpire® KT-880 GF20 is a high flow, 20% glass-fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaSpi.. |
|||
Flexural Strength | 238 MPa | 34500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON JX89626 PES LNP* STAT-KON* JX89626 is a compound based on Polyethersulfone containing Proprietary Fillers. Added feature of this material is: Electrically Conductive. |
|||
Flexural Strength | 238 MPa | 34500 psi | ASTM D 790 |
SABIC Innovative Plastics Valox® VC130 PBT (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Strength | 238 MPa | 34500 psi | ASTM D790 |
Techmer ES HiFill® PA6 GF35 HS L 35% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 35% Filler by WeightAdditive: Lubricant and Heat Stabilizer Features: Lubricated and Heat StabilizedProcessi.. |
|||
Flexural Strength | 238 MPa | 34500 psi | ASTM D790 |
Techmer ES Luriblend® PA6/6 GF33 TL10 HS 33% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 33% Filler by WeightAdditive: Heat Stabilizer and PTFE Lubricant(10%)Features: Lubricated, Good Wear Resistance, Heat Stab.. |
|||
Flexural Strength | 238 MPa | 34500 psi | ASTM D790 |
Techmer ES Luriblend® PA6/6 GF33 TL10 HS BK 33% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 33% Filler by WeightAdditive: Heat Stabilizer and PTFE Lubricant(10%)Features: Lubricated, Good Wear Resistance, Heat Stab.. |
|||
Flexural Strength | 238 MPa | 34500 psi | ASTM D790 |
Techmer ES Plaslube® J-1/30/TF/15 BK223 PA66 |
|||
Flexural Strength | 238 MPa | 34500 psi | ASTM D790 |
Techmer ES Plaslube® J-1/30/TF/15 RED PA66 |
|||
Flexural Strength | 238 MPa | 34500 psi | ASTM D790 |
Techmer ES Plaslube® J-1/30/TF/22 BK223 PA66 |
|||
Flexural Strength | 238 MPa | 34500 psi | ASTM D790 |
Techmer ES Plaslube® J-1/30/TF/22 NAT PA66 |
|||
Flexural Strength | 238 MPa | 34500 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP OF006A PPS (Europe-Africa-Middle East) LNP* Thermocomp* OF-1006 is a compound based on Polyphenylene Sulfide resin containing Glass Fiber. |
|||
Flexural Strength | 238 MPa | 34500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP QF007 PA 6/10 LNP* THERMOCOMP* QF007 is a compound based on Nylon 6/10 resin containing 35% Glass Fiber. |
|||
Flexural Strength | 238 MPa | 34500 psi | ASTM D790 |
Techmer ES Plaslube® J-1/30/TF/15 NAT PA66 |
|||
Flexural Strength | 238 - 265 MPa | 34500 - 38500 psi | |
Bulk Molding Compounds BMC T40(25)-XHS Die Casting Replacement Grade Molding Compound BMC T40(25)-XHS is a high strength molding compound with excellent dimensional stability. It is UL recognized and is available in a wide range of colors. Because of its superior physical propertie.. |