Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 17.2 MPa | 2500 psi | ASTM D790 |
Quadrant EPP Fluorosint® 135 PTFE and PPS Blend, with Proprietary Lubrication Fillers (ASTM Product Data Sheet) Chemical resistance parallels PTFE Continuous use temperatures to 500°F (260°C) Compared to PTFE higher load carrying capability 1/9 of the deformation under load lower coefficient of thermal exp.. |
|||
Flexural Strength | 17.2 MPa | 2500 psi | ASTM D790 |
Quadrant EPP Fluorosint® HPV Mica-filled PTFE (ASTM Product Data Sheet) |
|||
Flexural Strength | 17.2 MPa | 2500 psi | ASTM D790 |
Quadrant EPP Symalit® PFA Tetrafluoroethylene-perfluoroalkylvinylether (ASTM Product Data Sheet) |
|||
Flexural Strength | 17.2 MPa | 2500 psi | ASTM D790 |
Quadrant EPP TIVAR® Oil Filled UHMW-PE FDA/USDA Oil-Filled UHMW-PE (ASTM Product Data Sheet) |
|||
Flexural Strength | 17.2 MPa | 2490 psi | ASTM D790 |
PolyOne Maxxam™ FR PE 152 Polyethylene, Unspecified (PE, Unspecified) Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V.. |
|||
Flexural Strength | 17.2 MPa | 2490 psi | Perpendicular to pressing direction |
Momentive Performance Materials HBC Hot-Pressed Boron Nitride Hot-pressed BN is compacted at temperatures up to 2000°C and pressures up to 2000 psi to form a dense, strong engineering material that is easily machined. It is available in standard and custom.. |
|||
Flexural Strength | 17.2 MPa | 2490 psi | Perpendicular to pressing direction |
Momentive Performance Materials HBT Hot-Pressed Boron Nitride Hot-pressed BN is compacted at temperatures up to 2000°C and pressures up to 2000 psi to form a dense, strong engineering material that is easily machined. It is available in standard and custom.. |
|||
Flexural Strength | 17.2 MPa @Thickness 3.20 mm |
2490 psi @Thickness 0.126 in |
ASTM D790 |
Supreme Petrochem SC 6501 Toughened Polystyrene Characteristics Excellent melt strength Extremely tough Easy printability Easy miscibility with most grades of polystyrene Processing Extrusion Thermoforming Injection MoldingApplications Impac.. |
|||
Flexural Strength | 17.2 MPa | 2500 psi | ASTM-F417 |
CoorsTek PolyGlyde™ 5400 Self-Lubricating Seal PolyGlyde seals offer low heat generation in high-friction and high-stress environments. These seals provide superior performance over traditional carbon materials: runs cooler – even in dry-runni.. |
|||
Flexural Strength | 17.2 MPa | 2500 psi | ASTM D790 |
Ecomass® 3620BX18 5% Borated Polyethylene (HDPE) 5% Borated Polyethylene (HDPE), Product Form - Pellets, No Pre-Drying RequiredProcessing Method: Injection Molding, Compression MoldingNeutron Shielding ApplicationsInformation provided by Technica.. |
|||
Flexural Strength | 17.2 MPa | 2500 psi | |
Cotronics Resbond™ 954 High Temperature Ceramic Adhesive, Stainless Steel Composition |
|||
Flexural Strength | 17.2 - 20.0 MPa | 2490 - 2900 psi | |
Ceradyne Thermo-Sil® HS Fused Silica Fused Silica is an excellent thermal insulator with an extremely low coefficient of thermal expansion. It is excellent for thermal shock applications. The key characteristics of this material are:Hi.. |